1) Lamination defect
分层缺陷
1.
The characteristics, generating process and innuencing ractors of lamination defect of sendfinished pipe are analyzed based on pierced high temperature alloy blank, and the generating mechanism of lamination defect is discussed.
以高温合金管管坯穿孔为基础，对毛管分层缺陷的特征、形成过程及影响因素进行了研究，并讨论了分层缺陷的形成机理。
2.
The results show that the elements segregation was the main reason for the lamination defect During the continuous casting process,inclusions of MnS,TiC,NbC were formed because of elements segregation of S,Mn,Nb,Ti at the center of the steel.
Q345B中厚钢板在拉伸试验后断口出现分层现象,选择分层缺陷严重的部位,采用光学显微镜、扫描电镜、能谱仪等对其显微组织、缺陷形态和微区成分进行了分析。
2) lamination defects
分层缺陷
1.
The purpose of this project is aimed to analyze systematically the causes of the lamination defects in Q690D medium plate,The lamination defects of Q690D medium plate was studied by means of scanning electron microscopy and energy spectrum analysis.
采用扫描电镜及能谱分析等手段对Q690D钢分层缺陷进行了分析。
3) Annular lamination defect
环状分层缺陷
5) coating defect
涂层缺陷
1.
The effect of coating defect on the permeation behavior of corrosive ions through coatings,coatings degradation,the corrosion behavior of substrates are discussed based on the review of the study field which included coating defects,blistering and wet adhesion etc.
通过对涂层缺陷、涂层起泡、湿附着力等研究领域的回顾 ,讨论了涂层缺陷对腐蚀性介质离子在涂层中的传输行为、涂层失效、基体腐蚀行为等方面的影响。
6) coating defects
涂层缺陷
1.
The influence of soil resistivity and coating defects on IR drop error in cathodic protection(CP)potential measurement was studied by theoretical methods.
理论分析土壤电阻率和涂层缺陷电阻等参数对埋地管道阴极保护电位测量时IR降误差的影响 ,建立IR降电阻因子计算模型 ,并用实验数据验证 ,此外 ,还讨论了IR降误差的工程预测方法 。
补充资料：点缺陷(见晶体缺陷)
点缺陷(见晶体缺陷)
point defect
点缺陷point defeet见晶体缺陷。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条