1) Nd_2Fe_14 B/α-Fe nanocomposite
Nd2Fe14B/α-Fe纳米晶复相
2) nanocomposite Nd2Fe14B/α-Fe
纳米晶复相Nd2Fe14B/α-Fe
1.
Nearly compact permanent magnets of nanocomposite Nd2Fe14B/α-Fe were prepared by powder hot extrusion of canned cold-pressed compacts in vacuum with cold pressing powders of amorphous Nd2Fe14B and α-Fe.
将球磨后获得的Nd2Fe14B非晶相和α-Fe纳米晶直接进行冷压制坯、真空包套、粉末热挤压来制备近致密的纳米晶复相Nd2Fe14B/α-Fe永磁体。
3) nanocrystalline multiphase (Nd2Fe14B/α-Fe) permanent magnet
纳米晶复相(Nd2Fe14B/α-Fe)永磁体
4) Nd_2Fe_(14)B/α-Fe nanocomposite
Nd2Fe14B/-αFe纳米复相
5) Nd2Fe14B/α-Fe composite magnets
Nd2Fe14B/α-Fe复合磁体
1.
Isotropic Nd2Fe14B/α-Fe composite magnets were prepared by powder blending and spark plasma sintering technique.
采用粉末混合技术和放电等离子烧结制备出各向同性Nd2Fe14B/α-Fe复合磁体。
6) nanocrystal α-Fe(Si)
纳米晶α-Fe(Si)
补充资料：particle reinforced Fe-matrix composite
分子式：
CAS号：
性质：铁或铁合金基体以TiC和WC等碳化物、TiN等氮化物、TiB2等硼化物颗粒增强复合材料。其耐磨性、抗蚀性和热性能良好，硬度高，广泛用于磨削工具材料和耐磨结构部件。经烧结而成的颗粒增强铁基复合材料的性能为：硬度可高达300GPa，工作温度可达1000℃。制造方法主要有粉末冷压法、热压法和热等静压法，烧结温度在1000～1600℃之间。烧结而成的复合材料的性能依基体和增强体百分数不同而不同。在切削工具和耐磨部件中，铁基体含量通常在50％～70％之间，而在某些耐高温耐磨损部件的金属陶瓷中，铁含量可少至百分之几。
CAS号：
性质：铁或铁合金基体以TiC和WC等碳化物、TiN等氮化物、TiB2等硼化物颗粒增强复合材料。其耐磨性、抗蚀性和热性能良好，硬度高，广泛用于磨削工具材料和耐磨结构部件。经烧结而成的颗粒增强铁基复合材料的性能为：硬度可高达300GPa，工作温度可达1000℃。制造方法主要有粉末冷压法、热压法和热等静压法，烧结温度在1000～1600℃之间。烧结而成的复合材料的性能依基体和增强体百分数不同而不同。在切削工具和耐磨部件中，铁基体含量通常在50％～70％之间，而在某些耐高温耐磨损部件的金属陶瓷中，铁含量可少至百分之几。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。