1) common sintered clay brick
烧结普通粘土砖
2) Common clay brick
普通粘土砖
3) fired common brick
烧结普通砖
1.
The fault of using nonstandard fired common brick and its prevention measures;
使用非标准烧结普通砖的危害及防止措施
2.
By carrying out single-side shear bonding experiments between 63 pieces of fired common brick and fiber reinforced polymers(FRP),including carbon fiber reinforced polymers(CFRP) and grass fiber reinforced polymers(GFRP),the whole course of the shear bonding failure and failure characteristic between FRP and brick are analyzed.
通过63块烧结普通砖与碳纤维布(CFRP)、玻璃纤维布(GFRP)的单面剪切试验,分析纤维增强复合材料(FRP)与烧结普通砖粘结破坏的全过程及破坏特征。
3.
This paper has conducted research on the effective bond length between FRP and fired common brick by test.
论文通过试验对纤维布(Fiber Reinforced Polymer,简称 FRP)与烧结普通砖之间剥离破坏的有效粘结长度进行了研究。
4) common fried brick
普通烧结砖
5) agglutination loam brick
烧结粘土砖
6) non-baked brick
非烧粘土砖
补充资料：粘土砖
以粘土熟料作骨科,耐火粘土作结合剂制成的Al2O3含量为30～48％的耐火材料制品。粘土砖是历史最久、应用最广泛的耐火材料。70年代中国粘土砖产量约占耐火材料总产量的65%左右，美、英、日等国约占40～50%。制造粘土砖的原料是粘土质矿物。天然耐火粘土一般可分为硬质粘土和软质粘土。在耐火材料制造工艺中，前者大多数经煅烧后用作熟料；后者加水后，塑性好，容易烧结，多用作结合剂。中国山东等地焦宝石(硬质)和苏州粘土(软质)都是中外闻名的优质耐火粘土。粘土矿物主要有高岭石(Al2O3·2SiO2·2H2O)、地开石(成分与高岭石相同,但晶格常数不同)、蒙脱石(Al2O3·4SiO2·6H2O)和云母类矿物。
中国的粘土砖Al2O3含量一般多在40％以上，Fe2O3含量小于2.0～2.5％。配料中熟料为65～85％，结合粘土为35～15％。将粉碎的结合粘土和磨细的熟料混磨,再与颗粒熟料一起配制成半干泥料,高压成型,在约1400℃下烧成，性能较好。粘土砖在高温下呈弱酸性，抗碱性熔渣侵蚀的能力稍差,但随Al2O3含量提高而增强。热稳定性较硅砖、镁砖（见镁质砖）等为好。
粘土质耐火材料原料丰富，加工简便,价格低廉,因此比其他任何耐火材料使用得更为广泛：用于高炉、热风炉、化铁炉、盛钢桶及浇钢系统和均热炉,加热炉,有色金属熔炼炉，硅酸盐工业和化学工业用窑炉以及所有热工设备的烟囱和烟道等。
中国的粘土砖Al2O3含量一般多在40％以上，Fe2O3含量小于2.0～2.5％。配料中熟料为65～85％，结合粘土为35～15％。将粉碎的结合粘土和磨细的熟料混磨,再与颗粒熟料一起配制成半干泥料,高压成型,在约1400℃下烧成，性能较好。粘土砖在高温下呈弱酸性，抗碱性熔渣侵蚀的能力稍差,但随Al2O3含量提高而增强。热稳定性较硅砖、镁砖（见镁质砖）等为好。
粘土质耐火材料原料丰富，加工简便,价格低廉,因此比其他任何耐火材料使用得更为广泛：用于高炉、热风炉、化铁炉、盛钢桶及浇钢系统和均热炉,加热炉,有色金属熔炼炉，硅酸盐工业和化学工业用窑炉以及所有热工设备的烟囱和烟道等。