1) Uniform corrosion method of laboratory immersion test
均匀腐蚀全浸试验
2) Indoor immersion corrosion
室内全浸腐蚀试验
3) immersion corrosion test in sea water
海水全浸腐蚀试验
4) immersion corrosion experiment
浸渍腐蚀试验
1.
The contact corrosion mechanism of copper galvanically coupled with carbon is studied by the rotating disc electrode (RDE) method, immersion corrosion experiments and X-ray diffraction analysis.
应用旋转圆盘电极(RDE)法、浸渍腐蚀试验法及腐蚀表面的X射线衍射分析法研究了3%NaCl溶液中碳-铜短路接触腐蚀的机理。
5) general corrosion
均匀腐蚀
1.
Corrosion behaviors of austenite stainless steel 1Cr18Ni9Ti in sodium carbonate containing uranium were studied by electrochemical polarization and general corrosion methods.
用动电位极化法和均匀腐蚀法研究了奥氏体不锈钢 (1Cr18Ni9Ti)在含铀碳酸钠溶液中的腐蚀行为。
2.
5%-6% NaCl solutions and a similar general corrosion resistance in -0.
5mol／LH2SO4溶液中具有相当于原始不锈钢的耐均匀腐蚀性能。
6) Uniform Corrosion
均匀腐蚀
1.
Calculation on Remaining Life of Buried Crude Pipeline in Uniform Corrosion;
埋地输油管道均匀腐蚀剩余寿命计算
2.
Anti-uniform corrosion property of theses materials are measured under 270℃and 290℃.
本文选用压力容器常用钢——— 12CrMoV、2 0 g、16MnR三种材质 ,按照适于我国一水硬铝石型铝土矿的双流法溶出工艺条件 ,在铝土矿溶出实验用的钢弹中 ,测定了 2 70℃、2 90℃温度下三种材质的耐均匀腐蚀性。
3.
Under the water chemistry condition simulating pressurized water reactors(PWRs) coolant(temperature,345 ℃;B,800 mg/L;Li,2 mg/L), their stress corrosion and uniform corrosion behaviors are studied.
采用GB43 3 4 7 84和法国RCC MMC1 3 1 0对国产两种堆焊材料进行了点腐蚀、晶间腐蚀试验 ,在模拟压水堆核电站介质 (温度 3 45℃ ,80 0mg/LB ,2mg/LLi)条件下 ,研究了堆焊材料的应力腐蚀和均匀腐蚀性能。
补充资料：均匀腐蚀
分子式：
CAS号：
性质：在金属表面的全部或大部普遍地发生化学或电化学反应，也称为全面腐蚀。是一种危害性最小的腐蚀形态。在这种腐蚀情况下，金属以一种可接受的腐蚀速率被均匀地溶解掉。通常用平均腐蚀率作为衡量腐蚀的程度，也可作为选材的依据。一般要求年腐蚀率低于1～1.5mm。
CAS号：
性质：在金属表面的全部或大部普遍地发生化学或电化学反应，也称为全面腐蚀。是一种危害性最小的腐蚀形态。在这种腐蚀情况下，金属以一种可接受的腐蚀速率被均匀地溶解掉。通常用平均腐蚀率作为衡量腐蚀的程度，也可作为选材的依据。一般要求年腐蚀率低于1～1.5mm。