1) photocatalytic compound
复合体光催化剂
1.
Based on preparation of SnO_2 sol by sol-gel method,nano-meter photocatalytic compound of TiO_2/SnO_2 was prepared and the atom ratio of titanium to tin on the surface is 85∶15(by XPS analysis).
在采用溶胶-凝胶法制备SnO2溶胶的基础上,制备出表面Ti/Sn原子比为85∶15(XPS全谱分析)的TiO2/SnO2复合体光催化剂;用于硫磷农药废水的降解,试验结果表明:复合体光催化剂比单一TiO2催化剂的催化活性要高,其原因是由于复合TiO2/SnO2催化剂中SnO2可接收电子,减少了TiO2电子-空穴对的复合,从而提高其催化活性。
3) composite photocatalyst
复合光催化剂
1.
Preparation of TiO_2-Al_2O_3 composite photocatalyst and degradation of methyl orange
TiO_2-Al_2O_3复合光催化剂的制备及其对甲基橙的降解
2.
The nanosized composite photocatalysts of titania pillared montmorillonite were synthesized via solvothermal method by using water and ethanol as solvent,hexamethylene tetramine as precipitant and titanium trichloride as precursor.
结果表明,复合光催化剂具有良好的介孔结构,其孔径分布主要集中在6~10 nm,且比表面积明显增大。
3.
Iron doping TiO2/bentonite composite photocatalyst were prepared by sol-gel method.
采用酸性溶胶法制备掺铁-TiO2/膨润土复合光催化剂,利用XRD、IR等测试手段对其进行了表征。
4) coupled photocatalyst
复合光催化剂
1.
Preparation and characterization of CeO_2/TiO_2 coupled photocatalyst;
复合光催化剂CeO_2/TiO_2的制备及性能研究
2.
RuO_2/La_2O_3/TiO_2 coupled photocatalyst was prepared by the sol-gel-immersion process with Ti(OC_4H_9)_4 as a precursor.
钛酸丁酯为前驱体,采用溶胶凝胶浸渍法制备RuO2 /La2O3 /TiO2 复合光催化剂,以紫外灯为光源,研究了催化剂组成、煅烧温度、溶液pH值等因素对直接耐晒黑G(DFBG)光催化降解的影响。
6) Multi TiO 2 photocatalysts
复合TiO2光催化剂
补充资料：复合催化剂BA-3
分子式：
分子量：
CAS号：
性质：白色结晶，溶于水。系树脂整理高效催化剂，用于纺织印染树脂整理。使用配方为复合催化剂BA-3 0.11千克，渗透剂JFC 0.5千克，柔软剂VS 10千克，45%的树脂2D（二羟甲基二羟基乙烯脲）50千克，用水稀释到一定体积使用。由氟硼酸钠和柠檬酸铵复合而成。
分子量：
CAS号：
性质：白色结晶，溶于水。系树脂整理高效催化剂，用于纺织印染树脂整理。使用配方为复合催化剂BA-3 0.11千克，渗透剂JFC 0.5千克，柔软剂VS 10千克，45%的树脂2D（二羟甲基二羟基乙烯脲）50千克，用水稀释到一定体积使用。由氟硼酸钠和柠檬酸铵复合而成。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条