1) thermo-mechanical processing
机械热处理
1.
In order to investigate the effects of the pre-deformation on second phase particles and recrystallization of AA2195 Al-Li alloy, cold-rolling pre-deformation prior to overaging was exploited in the traditional thermo-mechanical processing for grain refinement.
在细化晶粒的传统机械热处理工艺中的过时效前引入冷轧预变形,研究预变形对AA2195铝锂合金过时效第二相粒子组态及最终再结晶组织的影响。
2.
The effects of pre-deformations and overaging on grain refinement of AA2195 Al-Li alloy in thermo-mechanical processing (TMP) were investigated by means of optical microscopy (OM) and scanning electron microscopy (SEM).
通过金相和扫描电镜等分析手段,研究预变形和过时效对机械热处理细化AA2195铝锂合金晶粒的影响。
3.
Fine grained Al-Mg-Li alloy sheets were produced by thermo-mechanical processing.
采用机械热处理法制备Al-Mg-Li合金细晶板材,研究预热温度、中间退火温度及转向轧制对板材塑性开裂及晶粒细化的影响。
2) thermomechanical processing
机械热处理
1.
The superplasticity of 01420 Al-Li alloy was studied by means of simple tension,and good superplasticity of the alloy was found after suitable thermomechanical processing.
采用单向拉伸对01420Al-Li合金进行超塑性研究,发现该合金经过适当的机械热处理后能获得良好的超塑性。
2.
This paper details the influence of thermomechanical processing (TMP) on the microstructures and mechanical properties of TC21 titanium alloy, a new alpha+beta alloy with high strength, ductility and toughness developed in China.
TC21合金是我国自行研制的一种新型高强高韧两相钛合金，本文主要对合金机械热处理工艺、微观组织和室温机械性能之间的关系作了系统的研究。
3) TMCP
机械热处理
1.
The Development of TMCP and Relaxation-Precipitation-Control Transformation(RPC) Technology;
机械热处理工艺的发展及弛豫—析出—控制相变技术
2.
By a special thermomechanical control process(TMCP-RPC), relaxation for a certain time after control rolling and then direct quenching/accelerated cooling, the strain induced precipitions and defect structure in deformed austenite resulted in refinement of intermediate transformation microstructure.
利用一种特殊的机械热处理工艺技术，即在控轧终轧后经过一段控制时间与温度的 弛豫，使得基体中出现应变诱导析出以及变形奥氏体中缺陷组态重组，在随后的直接淬火或加 速冷却过程中，获得细化的板条贝氏体／马氏体组织。
4) thermomechanical processing
热机械处理
1.
An(α2+O+B2) three-phase Ti3Al-based alloy,designated as TD3 alloy,is presented,including the thermomechanical processing technology,the microstructure control and the mechanical properties of some typical microstructures of TD3 alloy bars and forgings.
本文介绍了一种中等Nb含量的(α2+O+B2)三相Ti3Al基合金(TD3合金)的热机械处理工艺和微观组织特征,以及典型组织的力学性能,并与一些典型的O相基合金,高温钛合金,高温合金进行了对比。
2.
The effect of thermomechanical processing (TMP) on the morphologies and room temperature tensile properties of lath microstructure in Ti 3Al based alloy, Ti 24Al 14Nb 3V(at%), has been studied.
研究了热机械处理（ＴＭＰ）对Ｔｉ３Ａｌ基合金Ｔｉ－２４Ａｌ－１４Ｎｂ－３Ｖ（原子分数，％）板条组织的形貌及室温拉伸性能的影响。
5) thermo-mechanical treatment
热机械处理
1.
The effect of thermo-mechanical treatment on microstructure and properties of CuCrZrBeRE alloy and strengthening mechanism were studied.
研究了热机械处理对CuCrZrBeRE合金组织及性能的影响 ,探讨了合金的强化机理。
6) low temperature thermo-mechanical treatment
低温热机械处理
1.
hot rolling and low temperature thermo-mechanical treatment, and possessed tensile strength σb= 625 MPa, electric conductivity a = 82.
6％Al铸造合金,经锻造、热轧和低温热机械处理后的0。
补充资料：金属热处理:真空热处理
将金属工件在 1个大气压以下(即负压下)加热的金属热处理工艺。20世纪20年代末﹐随著电真空技术的发展﹐出现了真空热处理工艺﹐当时还仅用於退火和脱气。由於设备的限制﹐这种工艺较长时间未能获得大的进展。60～70年代﹐陆续研製成功气冷式真空热处理炉﹑冷壁真空油淬炉和真空加热高压气淬炉等﹐使真空热处理工艺得到了新的发展。在真空中进行渗碳﹐在真空中等离子场的作用下进行渗碳﹑渗氮或渗其他元素的技术进展﹐又使真空热处理进一步扩大了应用范围。
特点 金属零件在真空中的热处理能防止氧化脱碳并具有脱气效应﹐但金属元素可能蒸发。
防止氧化脱碳 真空热处理炉的加热室在工作时处於接近真空状态﹐仅存在微量一氧化碳和氢气等﹐它们对於加热的金属是还原性的﹐不发生氧化脱碳的反应﹔同时还能使已形成的氧化膜还原﹐因此加热后的金属工件表面可以保持原来的金属光泽和良好的表面性能。
脱气效应 金属零件在真空环境中加热时﹐金属中的有害气体﹐例如鈦合金中的氢和氧﹐会在高温下逸出﹐有利於提高金属的机械性能。
金属元素蒸发 各种元素都有自身的蒸气压﹐如果环境中的压力低於某种元素的蒸气压﹐这种元素就会蒸发。在真空热处理时﹐应根据钢中所含合金元素的蒸气压来选择加热时的真空度或温度﹐以避免合金元素蒸发。
工艺 真空热处理可用於退火﹑脱气﹑固溶热处理﹑淬火﹑回火和沉淀硬化等工艺。在通入适当介质后﹐也可用於化学热处理。
真空中的退火﹑脱气﹑固溶处理主要用於纯净程度或表面质量要求高的工件﹐如难熔金属的软化和去应力﹑不锈钢和镍基合金的固溶处理﹑鈦和鈦合金的脱气处理﹑软磁合金改善导磁率和矫顽力的退火﹐以及要求光亮的碳钢﹑低合金钢和铜等的光亮退火。真空中的淬火有气淬和液淬两种。气淬即将工件在真空加热后向冷却室中充以高纯度中性气体(如氮)进行冷却。适用於气淬的有高速钢和高碳高铬钢等马氏体临界冷却速度较低的材料。液淬是将工件在加热室中加热后﹐移至冷却室中充入高纯氮气并立即送入淬火油槽﹐快速冷却。如果需要高的表面质量﹐工件真空淬火和固溶热处理后的回火和沉淀硬化仍应在真空炉中进行。
特点 金属零件在真空中的热处理能防止氧化脱碳并具有脱气效应﹐但金属元素可能蒸发。
防止氧化脱碳 真空热处理炉的加热室在工作时处於接近真空状态﹐仅存在微量一氧化碳和氢气等﹐它们对於加热的金属是还原性的﹐不发生氧化脱碳的反应﹔同时还能使已形成的氧化膜还原﹐因此加热后的金属工件表面可以保持原来的金属光泽和良好的表面性能。
脱气效应 金属零件在真空环境中加热时﹐金属中的有害气体﹐例如鈦合金中的氢和氧﹐会在高温下逸出﹐有利於提高金属的机械性能。
金属元素蒸发 各种元素都有自身的蒸气压﹐如果环境中的压力低於某种元素的蒸气压﹐这种元素就会蒸发。在真空热处理时﹐应根据钢中所含合金元素的蒸气压来选择加热时的真空度或温度﹐以避免合金元素蒸发。
工艺 真空热处理可用於退火﹑脱气﹑固溶热处理﹑淬火﹑回火和沉淀硬化等工艺。在通入适当介质后﹐也可用於化学热处理。
真空中的退火﹑脱气﹑固溶处理主要用於纯净程度或表面质量要求高的工件﹐如难熔金属的软化和去应力﹑不锈钢和镍基合金的固溶处理﹑鈦和鈦合金的脱气处理﹑软磁合金改善导磁率和矫顽力的退火﹐以及要求光亮的碳钢﹑低合金钢和铜等的光亮退火。真空中的淬火有气淬和液淬两种。气淬即将工件在真空加热后向冷却室中充以高纯度中性气体(如氮)进行冷却。适用於气淬的有高速钢和高碳高铬钢等马氏体临界冷却速度较低的材料。液淬是将工件在加热室中加热后﹐移至冷却室中充入高纯氮气并立即送入淬火油槽﹐快速冷却。如果需要高的表面质量﹐工件真空淬火和固溶热处理后的回火和沉淀硬化仍应在真空炉中进行。