2) High Basicity High Al_2O_3 Slag
高碱度高Al_2O_3炉渣
1.
Behavour of Non-metallic Inclusions in Liquid Alloy Steel under High Basicity High Al_2O_3 Slag;
高碱度高Al_2O_3炉渣下合金钢液中非金属夹杂物的行为
3) blast furnace slag
高炉炉渣
1.
Alumina content in Nanjing Steel blast furnace slag is up to 19%,which results in worse slag fluidity,higher furnace operating temperature and higher silicon content of hot metal.
南京钢铁集团公司高炉炉渣中氧化铝含量高达19%,因此炉渣流动性变差,高炉被迫采用高温操作,铁水硅含量偏高,影响了高炉的强化。
2.
The measurementand systemat-ic study had been made on chemical components,mineral compositions,mineral structure,viscosity and melting tem-perature of the blast furnace slag.
试验选取生产现场的高炉炉渣作为基准原料,对现场高炉炉渣和高炉初渣的化学成分、矿物组成、矿物结构以及粘度和熔化性温度进行了测定和系统研究。
3.
INBA is a new type of blast furnace slag processing technology,can be converted to high - grade blast furnace slag cement materials,the recycling of slag implementation.
INBA法是一种新型高炉炉渣处理技术,可以将高炉废渣转为高品位的水泥原材料,实现炉渣的再生利用。
4) BF slag
高炉炉渣
1.
The metallurgic characteristic of Tanggang BF slag was researched in laboratory onthe basis of the current production parameters in the paper.
本文以唐钢高炉生产条件为基础,对唐钢高炉炉渣的冶金性能进行了实验室研究,分析CaO/SiO_2、Al_2O_3、MgO 这三个因素对炉渣的冶金性能产生的重要影响,建立其冶金性能的数学模型,并得出炉渣在高Al2O3条件下合理的造渣制度。
5) blast furnace slag
高炉炉渣<冶>
6) blast furnace slag
高炉矿渣
1.
A large quantity of blast furnace slag discharged in Laiwu Steel Company causes serious environmental pollution.
莱钢每年排放大量的高炉矿渣造成了严重的环境污染,利用高炉矿渣生产微晶玻璃受到国内外的广泛关注。
2.
Replacement of pebbles with blast furnace slag for roadbed and road base cannot only solve the problem of transportation and construction cost,but can solve the problem of pollutions caused by abandoned blast furnace slag,which is significant for the alleviating material shortage,increasing the value of slag,comprehensive utilization and protection of the ecological environment.
高炉矿渣代替碎(卵)石作为公路路基、路面基层材料既可解决材料运距长、建设成本高的问题,又能解决被废弃高炉矿渣占用大量土地资源并对环境造成严重污染的问题,对缓解路用材料短缺,提高矿渣价值和综合利用率,以及保护生态环境等方面具有重大意义。
3.
In view of both the understanding of the double-interface sealing system and the basic analysis of the chemical and physical properties of blast furnace slag(BFS),a set of experimental facilities was developed for the simulation of interfacial bonding in cementing,and experimental evaluation was conducted on the performance of blast furnace slag cement system by bond strength simulation test.
基于对双界面封固系统的认识和对高炉矿渣物化特性的分析,研制了用于模拟固井界面胶结的试验装置,利用胶结强度模拟试验等方法评价了高炉矿渣水泥体系的性能。
补充资料:高炉渣的利用
高炉炼铁中由加入炉的矿石中的脉石、焦炭的灰分同熔剂反应熔化形成的副产物,是含有多种氧化物的复杂硅酸盐,常含有少量硫化物、氟化物和碳化物等。它的成分和产量因高炉原料和燃料的成分而有所不同。冶炼每吨铁生成的渣量(即渣铁比),大致为300~600公斤。高炉渣的主要成分为:CaO35~40%,SiO232~42%,Al2O36~16%,MgO4~13%,还含有少量MnO、FeO和S等。高炉渣的比重:液态2.2~2.5,固态2.3~2.7;出炉熔渣温度1400~1550℃,每公斤含热量400~460千卡。
熔融的高炉渣经缓冷、水淬和喷水等方法制成不同的建筑产品。
高炉渣的利用在美、日、法、英、联邦德国等国,基本上达到排渣和利用平衡,苏联1975年高炉渣的利用率达78.5%。中国目前每年约排出高炉渣2100万吨,约70%制成水渣,用作水泥原料,少量用作道碴和膨珠。
熔融的高炉渣经缓冷、水淬和喷水等方法制成不同的建筑产品。
高炉渣的利用在美、日、法、英、联邦德国等国,基本上达到排渣和利用平衡,苏联1975年高炉渣的利用率达78.5%。中国目前每年约排出高炉渣2100万吨,约70%制成水渣,用作水泥原料,少量用作道碴和膨珠。