1) segregation Hopkinson shock pressure bar
分离式Hopkinson冲击压杆装置
1.
In order to determine the dynamic performance of 32CrMo4 steel used in the gun body of the composite perforation gun under the downhole high temperature condition and the working environment of high loading rate, the single-axial dynamic compression test was carried out by using MTS testing machine and segregation Hopkinson shock pressure bar equipment at the strain rates of 0.
为确定复合射孔枪枪身材料32CrMo4钢在井下高温、高加载率工作环境下的动态性能,利用MTS试验机和分离式Hopkinson冲击压杆装置做了应变率为0。
2) SHPB(split Hopkenson pressure bar)
分离式Hopkinson压杆装置
3) split Hopkinson pressure bar apparatus
分离式Hopkinson压杆试验装置
1.
The details of an experiment using a 100-mm-diameter split Hopkinson pressure bar apparatus are presented.
采用φ100mm分离式Hopkinson压杆试验装置,研究了玄武岩纤维混凝土在冲击荷载作用下的动态力学性能,并将其与相同纤维掺量的碳纤维混凝土的冲击力学性能进行对比分析。
4) triaxial split Hopkinson pressure bar
三轴分离式Hopkinson压杆装置
5) split Hopkinson pressure bar(SHPB)
分离式Hopkinson压杆
1.
Experiments with strain rate varying from 101 s-1 to103 s-1 on granite and concrete under uniaxial compressive loading are conducted with the modified split Hopkinson pressure bar(SHPB).
采用黄铜波形整形器改进后的分离式Hopkinson压杆装置,分别对花岗岩和混凝土试件进行不同应变率(101～103)s-1下的单轴冲击压缩试验,有效地减少传统Hopkinson压杆试验中,岩石类脆性材料在内部应力达到均衡之前过早破坏以及输入波的高频震荡给试验数据带来的波动性。
2.
There exist three main problems in the split Hopkinson pressure bar(SHPB) technique of measuring the dynamic properties of concrete material,which are the restriction of nonuniform stress (strain),the dispersion in wave propagation due to the large-diameter SHPB,and the influence of initial rising point of stress wave.
根据实验和理论分析,目前分离式Hopkinson压杆装置(SHPB)间接测量混凝土材料动态应力—应变关系时主要存在三方面问题,分别是应力应变不均匀的限制、大尺寸SHPB压杆产生的应力波弥散及数据处理时应力波波头选取的影响。
3.
The Split Hopkinson Pressure Bar(SHPB) is an ideal tool in carrying out high-speedloading to quasi-brittle materials, it can afford many loading means loading means to mensurate materials properties under dynamic loading.
分离式Hopkinson压杆是对准脆性材料实施高速加载的理想工具,利用该装置可以对准脆性材料实施各种加载方式,测定材料的动力特性参数。
6) Split Hopkinson pressure bar
分离式Hopkinson压杆
1.
Dynamic tests were made at strain rate 10~2 s~(-1)～10~3 s~(-1) by split Hopkinson pressure bar(SHPB),with bullet speeds of 4 m/s～15 m/s,and semiconductor gage was used on the transmitted bar.
在分离式Hopkinson压杆(SHPB)上做了铜基粉末冶金摩擦材料在102s-1～103s-1应变率范围内的冲击试验,弹速范围为4m/s～15m/s,在透射杆上采用了半导体应变片技术;在MTS实验机上做了该材料在10-4s-1～10-3s-1应变率范围内的准静态实验,分别在应变为0 005,0 010,0 020,0 035时卸载再加载,以验证材料的黏弹塑性特征。
2.
The split Hopkinson pressure bar test equipment was improved through adopting multi-measures.
采取多种措施改进了分离式Hopkinson压杆试验技术,用改进的设备对三峡坝址处的花岗岩进行了大量的动态单轴压缩试验和劈裂试验,发现该岩石具有明显的应变率效应,其动态压缩破坏呈3种形态:边缘崩落、留心破坏、完全破坏;探讨了相应的破坏机制;分析了应变率对动态弹性模量和动态抗压强度的影响;以Hoek-Brown破坏准则为基础建立了相应的动态破坏准则。
3.
The split Hopkinson pressure bar with a diameter of 100mm and the Brazilian disc and the flattened Brazilian disc specimens subjected to diametral impact compression were used.
利用直径为100mm的分离式Hopkinson压杆径向冲击巴西圆盘和平台巴西圆盘试样,测试了大理岩在高应变率加载下的动态力学性能。
补充资料：冲击式钻机
冲击式钻机
percussion drilling machine
冲街燕笆致黑粼嚣蔽瘫层云井的水井钻机。按其结构形式不同，有钢丝绳冲击式钻机和潜孔振动冲抓锥。 钢绳冲击式钻机由机架、冲击机构、工具卷筒、桅杆、钻具等组成(图1)。工作时，由电动机经胶带驭动主轴，通过由冲击齿轮、曲柄连杆及冲击梁组成的冲击机构带动冲击梁往复摆动，牵引炯丝绳使钻头作上 图l冲击式钻机1.主钢丝绳;2.游轮;3.大胶带轮，4.胶带.5.电动机;6.1其卷筒;7.机架.8.主轴，9.机台木，10.井筒，n.操作手把;12.冲击齿轮:13.钻其，14.连杆，15.冲击轮，16.冲击梁;17.桅杆;18.天车下运动。当向下运动时，由于钻具的重t产生冲击力，以钻头破碎井底岩层，如此反复钻凿一定进尺后，再用抽砂筒将岩屑、泥沙、卵石等打捞出来。由于这种钻机冲击钻进时一般只是向并口加水或加不同浓度的泥浆而不需用泵抽吸，因此结构简单，容易制造，造价低，适宜在各种粘土、砂砾石、卵石等地层钻凿深度不超过300米，孔径500一600毫米的水井。 冲击机构主要由冲击齿轮曲柄连杆机构及冲击梁组成。冲击齿轮上有5个偏心的曲柄销孔，通过改变曲柄销的位t可以得到不同的冲程(每次冲击时钻具下落的距离).冲击梁由压绳滑轮、导向滑轮、游轮轴组成。冲程由钻具的质量、工作深度及所需的时间确定。通常取O，5一1米，冲击频率即每分钟钻具冲击次数，取决于钻具下落时曲柄旋转角、钻具在井孔中下落加速度和冲程，常用频率为so一50次/分。由于钻进时遇到阻力，钻具下落加速度要比重力加速度降低30%，一般软岩层为4.5一5米/秒2，硬岩层为6一6.5米/秒2。 冲击钻具有两种类型，一种是将钻头和钻杆固定在一起，用于凿进。而另设抽砂筒(底部有止逆阀的圆柱形筒)，换装后用来清除井底岩屑。这种钻具的钻杆为圆钢，按井的规格不同而取不同尺寸，一般长为2一6米，直径为112一188毫米，重量为145一704千克，其钻头的结构形式有补焊一字形钻头(刃口为一字形)和十字形钻头(刃口带副刃呈十字形);为增强钻头耐磨性，提高钻进速度，常采用钨钢粉补焊钻头刃口部。另一种是抽砂筒钻头，即把钻头和抽砂筒直接连接起来，边冲击凿进，边装砂，装满后抽出井外，适用于松散地层的钻进。抽砂筒的简壁有6一10条轴向肋骨，以减少提升时的阻力;有的在抽砂筒底部加上环刃，用于松散砂砾层钻并。 潜孔振动冲抓锥一种放人井孔内的电动机和钻具连成一体，靠振动、冲击作用破碎岩层的钻机。