1) curing rate
固化速度
1.
Effects on the curing rate of ultraviolet-curable waterborne system;
水性紫外光固化体系中光固化速度的影响因素
2.
Study on the effect of factors on curing rate of photosensitive resin in Stereo Lithography
SL中光敏树脂固化速度的影响因素研究
3.
The influence of pigment particals and photoinitiators and technical conditions on the curing rate of UV-cured offset ink was researched,and the photoinitiators compositions which has higher curing rate to the ink are proposed.
研究了颜料体系,引发体系和工艺条件对紫外光固化胶印油墨固化速度的影响,得出了与紫外光源和颜料相适应的引发速度较快的引发体系组合。
2) curing speed
固化速度
1.
A series of the UV cured films were prepared for analyzing the influences upon the UV curing speed, in terms of ammonia concentration, photoinitiator variation and loading, drying condition, neutralization degree and crosslinking agents variation.
制备了一系列紫外光固化树脂膜,考察了氨水浓度、光引发剂种类、用量、干燥条件、中和度、交联剂对光固化速度的影响。
2.
The effects of NCO group content and catalyst type on improving curing speed and hardness of the sealant were studied.
介绍了一种新型单组分聚氨酯密封胶;研究了预聚体中-NCO含量和催化剂种类对提高密封胶固化速度和硬度的影响;确定了制备工艺和配方。
3) curing velocity
固化速度
1.
Study on photosensitizer affecting UV-curing velocity;
紫外固化中光敏促进剂对固化速度的影响
2.
It shows that the content of photoinitiator, dilution and photosensitizer affects the curing velocity a lot .
本文研究了光引发剂、稀释剂对 191#不饱和聚酯树脂紫外光固化速度的影响。
4) solidification rate
凝固速度
1.
Influence of solidification rate on solid-liquid interface in unidirectional solidification microstructure of austenitic stainless steel
凝固速度对奥氏体不锈钢定向凝固组织及其固液界面稳定性的影响
2.
The percentage of RE in the matrix increases with the increase of solidification rate; the carbides in directional solidification microstructure are refined by RE added in high chromium cast iro.
研究表明,稀土主要位于高铬铸铁的基体组织中,随凝固速度的增加,稀土在基体中的含量增加;稀土对高铬铸铁定向凝固组织中的碳化物具有细化作用,并随凝固速度的增加,定向凝固高铬铸铁组织细化程度提高,同时稀土的加入使高铬铸铁的抗拉强度明显提高。
3.
The microstructure and its evolution of directionally solidified Cu-Cr alloy were investigated under the condition of different solidification rates,by use of optical microscope and SEM.
在高梯度定向凝固装置上制备Cu-1·0%Cr(质量分数)合金,用金相显微镜、扫描电镜进行微观组织的观察,研究定向凝固速度对Cu-Cr合金微观组织形貌的影响。
5) particle velocity
固粒速度
补充资料：120固化剂
N-羟乙基乙二胺又称β-羟乙基乙二胺，俗称120固化剂，结构式H2N(CH2)2NH(CH2)2OH，分子量92．06。无色或淡黄色透明粘性液体，微有氨气味。呈强碱性。有吸湿性。与水、乙醇混溶，微溶于乙酸。能从空气中吸收二氧化碳。低毒．LD504032mg／kg。
用作环氧树脂的室温快速固化剂，参考用量16～18phr，固化条件RT／10h或80℃／3h。
贮存于阴凉、干燥的库房内，防潮。
用作环氧树脂的室温快速固化剂，参考用量16～18phr，固化条件RT／10h或80℃／3h。
贮存于阴凉、干燥的库房内，防潮。