1) spin-coating
旋涂
1.
Fabrication of PZT thick film by two spin-coating methods based on Sol-Gel
基于溶胶-凝胶的两种旋涂方法制备PZT厚膜(英文)
2.
The influence of processing parameters in spin-coating was explored.
探索旋涂法制备工艺参数对薄膜结构的影响。
3.
The BaPbO3 thin films were deposited on aluminum oxide(Al2O3)substrates using the sol-gel method under spin-coating.
用溶胶-凝胶法在氧化铝(Al2O3)基片上旋涂成型BaPbO3薄膜。
2) spin coating
旋涂
1.
Evolvement model of photoresist spin coating thickness on spherical surface;
球面旋涂光刻胶膜厚分布的数学模型
2.
Using polymethyl methacrylate(PMMA) as the structure material,spin coating and dry etching technique are used to realize a structure integration of optical waveguide integrated circuit with cantilever-mass micro-machine structure on silicon substrate.
以聚甲基丙烯酸甲酯为结构材料,采用旋涂和干法刻蚀技术,实现了光波导集成光路和悬臂梁-质量块微机械结构在硅基底上的集成。
3.
By orthogonal design tests and analysis of variance methods, the effects of polymer concentration, spin velocity, spin acceleration and spin time on the film thickness are studied in process of spin coating.
采用正交试验设计 ,应用方差分析方法 ,研究了旋涂工艺中聚合物溶液的浓度、匀胶机的旋涂速度和加速度以及旋涂时间对所制备的薄膜厚度的影响。
3) spinning
[英]['spɪnɪŋ] [美]['spɪnɪŋ]
旋涂
1.
First SnCl2·2H2O and SbCl3 were dissolved with ethyl alcohol respectively,then nesa coatings were prepared with different ratio of Sb/Sn sols by different methods as such dipping-coating,spraying and spinning.
2H2O和SbCl3分别溶解于乙醇中,搅拌至完全溶解,以不同的Sb/Sb混合制备得到溶胶后,分别采用浸渍提拉、喷涂、旋涂工艺制备透明导电膜,并考察了不同制备工艺及热处理温度对膜的厚度、薄膜方块电阻以及对薄膜透光率的影响,运用XRD、SEM、TEM对所制备的透明导电膜进行了分析表征。
4) coating screen by spinning
旋涂法涂屏
5) spin-coating technology
旋涂技术
1.
Nanometer scale TiO_2 films are prepared on glass substrates with film thickness less than 100nm by sol-gel process combining with spin-coating technology.
采用溶胶-凝胶法,利用旋涂技术在玻璃表面制备了膜厚小于100nm的纳米TiO_2薄膜,以去离子水和苯作为水和油模型,利用XRD、AFM系统研究了煅烧温度、粒径及膜厚对薄膜双亲性的影响。
2.
Nanometer scale TiO2 film was prepared on glass substrate with film thickness less than 100 nm,crystal size in the range of 10~30 nm by sol-gel process combining with spin-coating technology.
以玻璃为基底,采用溶胶-凝胶法,利用旋涂技术在玻璃表面制备了膜厚小于100 nm,粒径在10~30 nm之间的纳米TiO2薄膜;利用XRD,AFM系统研究了煅烧温度及膜厚对薄膜亲水性的影响。
6) spin-coating method
旋涂法
1.
Bilayered and monolayered TiO2-KTaO3 films have been fabricated by sol-gel spin-coating method and heated at deferent temperature for an hour.
通过溶胶凝胶法和旋涂法制备了单层和双层TiO2-KTaO3薄膜,并在不同的温度下退火1h,研究了该薄膜的湿敏传感特性。
补充资料：旋涂
分子式：
CAS号：
性质：电子工业中，基片垂直于自身表面的轴旋转，同时把液态涂覆材料涂覆在基片上的工艺。
CAS号：
性质：电子工业中，基片垂直于自身表面的轴旋转，同时把液态涂覆材料涂覆在基片上的工艺。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。