1) TIG remelting technique
TIG重熔技术
2) TIG remelting
TIG重熔
1.
Affection of TIG remelting welding seam process on the residual stress in weld area;
TIG重熔工艺对焊缝区残余应力的影响
3) TIG surface remelting process
TIG表面重熔
1.
Compared with the conventional post grinding process for the weld layer,the effect of TIG surface remelting process on cavitation erosion resistance was investigated.
用氩弧熔化焊(M IG)在4020碳钢表面堆焊耐空泡腐蚀材料,然后采用TIG(钨极氩弧焊),将堆焊层改性;通过与传统磨削表面加工对比,研究了TIG表面重熔对空泡腐蚀的影响。
2.
Compared with grinding process,the effect of TIG surface remelting process on cavitation corrosion resistance was investigated.
采用TIG(钨极氩弧焊)表面重熔工艺对耐空泡腐蚀堆焊材料进行改性加工,与磨削表面加工对比研究了TIG表面重熔对空泡腐蚀的影响。
3.
Compared with grinding process,the effect of TIG surface remelting process to cavitation erosion resistance was investigated.
采用TIG(钨极惰性气体保护焊)表面重熔工艺对表面耐空泡腐蚀堆焊材料进行改性加工,与磨削表面加工对比研究了TIG表面重熔对空泡腐蚀的影响。
4) weld toe TIG remelting
焊趾TIG重熔
5) TIG welding technology
TIG焊接技术
1.
In order to develop the TIG welding technology suitable to AM50 magnesium alloy,the TIG welding performance of the alloy was studied.
为研究出一套适合于AM50的TIG焊接工艺,利用TIG焊接技术研究了AM50镁合金的焊接性,并调节工艺参数进行系统焊接试验,同时,对焊接接头也进行了相关的力学性能试验;试验结果表明:焊接电流、焊接速度和气体流量均对焊接接头表面成形性和力学性能产生重大影响,并得到一套完整的焊接工艺规范。
6) TIG building-up Technology
TIG堆积技术
补充资料：等离子电弧重熔
等离子电弧重熔
plasma arc remelting
熔(E SR)优点的等离子熔炼技术. 1963年美国联合碳化物(Union Carbide)公司下 属的林德(Linde)公司研制了两台实验型PAR炉，分 别装有1支和2支等离子体发生琴(即等离子枪)，均 采用立式水冷结晶器。同年，捷克斯洛伐克也用类似炉 子进行了试验研究。从70年代开始前苏联和日本等国 进行了大量的研究工作并将其应用于工业生产。乌克 兰巴顿电焊研究所在70年代就研制了PAR的系列设 备。最大炉子的功率为18ookw，采用6支等离子枪， 可生产直径达65omm的5t钢锭。日本大同特殊钢公 司于1972年开始进行PAR技术的试验，先后建成 25kg和50kg的试验炉并称之为PPC炉，1982年建成 了2t的工业炉。 设备主要包括1个或多个等离子枪、电极及其 升降装置、合金及其他炉料的加料装置、水冷铜结晶 器、抽锭装置、供水和供气系统、电源及供电回路等。图 1是两种典型的PAR炉的设备示意图。根据等离子气 体种类、电源和枪的种类，结晶器结构和安装方式的不 同具有不同的设备类型。图2归纳了PAR在设备及工 作条件的各种不同方式。等离子枪一般为转移弧型，可 采用直流、交流或在交流电上附加直流操作。由于枪内 阴极是钨及其合金制作，故通常是非自耗式的。中空阴 极自耗式枪和等离子电子束枪是两种特殊情况。大多 数PAR炉采用立式结晶器。也有的采用卧式结晶器或 带由旋转辊组成的卧式结晶器，其优点是可降低对炉 料的形状和化学成分的均匀性要求。