1) Fast firing
快速烧成
1.
The multi_component system R 2O(K 2O, Na 2O)-RO(CaO,MgO, ZnO)-Al 2O 3-B 2O 3-SiO 2 which fits for single fast firing cycle was adopted.
选择适合一次快速烧成的R2 O(K2 O ,Na2 O) -RO(CaO ,MgO ,ZnO) -Al2 O3-B2 O3-SiO2 系统 ,通过优化组成设计及物理化学过程的控制 ,实现了釉的自生分相乳浊 。
2.
The multi component system R 2O(K 2O,Na 2O) RO(CaO,MgO,ZnO)-Al 2O 3-B 2O 3 - SiO 2 which contains wide practical liquid liquid immiscibility region and fits for single fast firing cycle was adopted.
本研究选择具有大范围实用分相区、适合快速烧成的R2 O(K2 O ,Na2 O) -RO(CaO ,MgO ,ZnO) -Al2 O3-B2 O3-SiO2 系统 ,研究了该多元系统全熔块乳浊釉组成与结构间的相互关系。
2) fast-firing
快速烧成
1.
The necessity and the development of ceramic fast-firing technology were briefly reviewed, temperature distribution at cross sections in fast-firing ceramic tunnel kiln was described, and concrete measures of temperature equilibrium at cross sections in fast-firing ceramic tunnel kiln were offered.
简要说明了陶瓷工业实现快速烧成的必要性及其发展状况,介绍了快烧陶瓷隧道窑各烧成阶段的截面温度分布情况,提出了均衡陶瓷快烧隧道窑截面温度的具体措施。
3) fast firing,quick firing,rapid firing
快速烧成，快烧
4) rapid,firing kiln
快(速)烧(成)窑
5) Fast heat-treatment process
快速烧成工艺
6) low temperature and fast firing
低温快速烧成
补充资料：快速烧成
分子式：
CAS号：
性质：指制品的烧成周期从传统的数十小时缩短为数小时，数十分钟，甚至数分钟的迅速烧成。为了实现快速烧成，在工艺上:严格控制入窑水分，尽量减少坯体线收缩率，采用双面加热坯体，减少其自身的温差，合理控制烧成等措施。在窑炉上可采用小断面隔焰窑，使用高速等温烧嘴，进行急冷和强制通风，采用轻质材料筑窑。快速烧成可用于坯体的素烧和釉烧。其优点是生产效率高，燃料消耗少。如采用微波烧结等新技术，烧成周期将大大缩短，实现快速烧成则更为容易。
CAS号：
性质：指制品的烧成周期从传统的数十小时缩短为数小时，数十分钟，甚至数分钟的迅速烧成。为了实现快速烧成，在工艺上:严格控制入窑水分，尽量减少坯体线收缩率，采用双面加热坯体，减少其自身的温差，合理控制烧成等措施。在窑炉上可采用小断面隔焰窑，使用高速等温烧嘴，进行急冷和强制通风，采用轻质材料筑窑。快速烧成可用于坯体的素烧和釉烧。其优点是生产效率高，燃料消耗少。如采用微波烧结等新技术，烧成周期将大大缩短，实现快速烧成则更为容易。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。