1)  electrochemical protection
电化学保护
1.
Testing technique of electrochemical protection in oil and water well casing;
油水井套管的腐蚀及防护理论、实验与应用——油水井套管电化学保护测试方法
2.
The electrochemical protection mostly in terms of cathodic protection for steel reinforcing concrete structures aims to restrain or prevent the premature failure or damage of the structure due to corrosion of rebar.
综述了钢筋混凝土构筑物电化学保护的发展和现状 ,包括牺牲阳极系统和外加电流系统 。
3.
Effects of jnhibitors,electrochemical protection and alloy elements on the solution pH,cl oncentration,electrochemical stte,and corrosion rate inside pits,crevices and stress corrosion cracks were reviewed.
本文综述了缓蚀剂、电化学保护和合金元素三者对蚀孔、缝隙及裂缝内闭塞区腐蚀的影响,分析了局部腐蚀防止方法的作用机理。
2)  Electro chemical cathodic protection
电化学阴极保护
3)  electro-chemical protection
电化学保护作用
4)  electro chemical desalting protection
电化学脱盐保护
5)  coating-electrochemical protection
涂料-电化学保护
6)  chemical protection
化学保护
补充资料:电化学保护
电化学保护
electrochemical protection

   根据电化学腐蚀原理,依靠外部电流的流入改变金属的电位,从而降低金属腐蚀速度的一种材料保护技术。按照金属电位变动的趋向,电化学保护分为阴极保护和阳极保护两类。①阴极保护。通过降低金属电位而达到保护目的的,称为阴极保护。根据保护电流的来源,阴极保护有外加电流法和牺牲阳极法。外加电流法是由外部直流电源提供保护电流,电源的负极连接保护对象,正极连接辅助阳极,通过电解质环境构成电流回路。牺牲阳极法是依靠电位负于保护对象的金属(牺牲阳极)自身消耗来提供保护电流,保护对象直接与牺牲阳极连接,在电解质环境中构成保护电流回路。阴极保护主要用于防止土壤、海水等中性介质中的金属腐蚀。②阳极保护。通过提高可钝化金属的电位使其进入钝态而达到保护目的的,称为阳极保护。阳极保护是利用阳极极化电流使金属处于稳定的钝态,其保护系统类似于外加电流阴极保护系统,只是极化电流的方向相反。只有具有活化 - 钝化转变的腐蚀体系才能采用阳极保护技术,例如浓硫酸贮罐、氨水贮槽等。