1)  nano-structural ceramic
纳米结构陶瓷
2)  nanostructured ceramic coatings
纳米结构陶瓷涂层
1.
X ray measuring method for nanostructured ceramic coatings grinding surface residual stresses;
纳米结构陶瓷涂层的磨削表面残余应力的X衍射测定法
2.
We can obtain high quality nanostructured ceramic coatings in the metal substrate with HOVF,however,the grinding surface residual stresses produced correspondingly by the coatings' high strength and certain flexibility during the period of grinding treating.
在金属基体上用HOVF能获得高质量纳米结构陶瓷涂层,但涂层的高强度和韧性使其在磨削加工时产生表面残余应力。
3.
Studying progress of the surface residual stresses after grinding for nanostructured ceramic coatings;
目前,国外在纳米结构陶瓷涂层磨削表面残余应力的研究很少,我国正在对纳米陶瓷涂层材料超精密磨削后表面残余应力方面进行研究。
3)  nanostructured ceramic coating
纳米结构陶瓷涂层
1.
Nanostructured ceramic coatings is a novel class of engineering material in recent years, its fine properties make it have very extensive application perspective in industry.
纳米结构陶瓷涂层材料是近年来国内外迅速发展的一种新型的工程材料,其优良的性能使其在工程上有着极其广泛的应用前景。
2.
Nanostructured ceramic coatings, a kind of new engineering materials, are developed in recent years.
纳米结构陶瓷涂层材料是近年来研制出来的新型工程材料,在工业上有着广阔的应用前景。
4)  nano-vitrified bond
纳米陶瓷结合剂
1.
Development of a new nano-vitrified bond for superabrasive tools;
纳米陶瓷结合剂超硬磨具的制造工艺
5)  bulk nano-micron structured multiphase ceramics
纳米/微米结构块体复相陶瓷
1.
By adding ZrO_2(2Y) powder of certain content into (CrO_3+Al) combustion system, bulk nano-micron structured multiphase ceramics of Al_2O_3-35vol%ZrO_2 was obtained in one quick step through the SHS metallurgical process, and mirostructures and fracture behaviors of the multiphase ceramics were also investigated.
通过在(CrO3+Al)燃烧体系中添加一定量的ZrO2(2Y)粉末,利用SHS冶金技术直接制备出Al2O3-35vol%ZrO2纳米/微米结构块体复相陶瓷,研究该复相陶瓷的微观结构与断裂行为。
6)  nano-ceramics
纳米陶瓷
1.
In order to validate both oxidation phenomena of SiC nano powder during sintering and variety in properties of nano-ceramics after oxidation,Al2O3/SiC nanocomposite was fabricated through pressureless sintering in argon atmosphere and in air respectively.
为验证在空气环境中,烧结Al2O3/SiC纳米复合陶瓷过程是否出现纳米SiC粉料的氧化现象,以及氧化后纳米陶瓷性能的变化规律,分别采用了常压氩气保护烧结和常压空气环境中烧结两种工艺,制备了Al2O3/SiC纳米复合陶瓷。
2.
An effective method to prevent the aggregation and growth of nano-ceramics .
对共沉淀—凝胶法制备的氧化锆纳米陶瓷粉体,采用有机物液相悬浮法、弧光放电法、气相沉积法及粉体制备过程中直接包裹等方法对纳米氧化锆粉体进行表面包碳修饰,成功制备了包裹层厚度均匀、颗粒分散性好的碳包纳米氧化锆粉体,通过形貌观察、粒度测定、粉体烧结性能测试,探讨包裹层形成机理,为防止纳米陶瓷粉体的团聚长大探索有效途径。
3.
The research status of the multi-phase composite ceramic tool materials such as nano-ceramics, functionally gradient ceramics and zirconia ceramics are summarized primarily.
文章重点综述了纳米陶瓷、梯度复相陶瓷、氧化锆陶瓷等多相复合陶瓷刀具材料的研究现状 ,全面分析了陶瓷刀具材料的颗粒弥散增韧补强、纤维 (或晶须 )增韧、相变增韧及多种机理协同增韧等机制的研究动
补充资料:看纺织印染中应用纳米材料和纳米技术

纺织印染中应用纳米材料和纳米技术时,除了要解决纳米材料的制备技术之外,重要的是要解决好纳米材料的应用技术,其中关键问题是使纳米粒子和纺织印染材料的基本成分(即聚合物材料)之间处于适当的结合状态。印染中,纳米粒子在聚合物基体中的分散和纳米粒子在聚合物表面的结合是主要的应用技术问题。  


    制备聚合物/无机纳米复合材料的直接分散法,适用于各种形态的纳米粒子。印染中纳米粒子的使用一般采用直接分散法。但是由于纳米粒子存在很大的界面自由能,粒子极易自发团聚,利用常规的共混方法不能消除无机纳米粒子与聚合物基体之间的高界面能差。因此,要将无机纳米粒子直接分散于有机基质中制备聚合物纳米复合材料,必须通过必要的化学预分散和物理机械分散打开纳米粒子团聚体,将其均匀分散到聚合物基体材料中并与基体材料有良好的亲和性。直接分散法可通过以下途径完成分散和复合过程:  


    高分子溶液(或乳液)共混:首先将聚合物基体溶解于适当的溶剂中制成溶液(或乳液),然后加入无机纳米粒子,利用超声波分散或其他方法将纳米粒子均匀分散在溶液(或乳液)中。有人将环氧树脂溶于丙酮后加入经偶联剂处理过的纳米TiO2,搅拌均匀,再加入 40wt%的聚酰胺后固化制得了环氧树脂/TiO2纳米复合材料。还有人将纳米SiO2粒子用硅烷偶联剂处理后,改性不饱和聚酯。  


    熔融共混:将纳米无机粒子与聚合物基体在密炼机、双螺杆等混炼机械上熔融共混。如将PMMA和纳米SiO2粒子熔融共混后,双螺杆造粒制得纳米复合材料。又如利用偶联剂超声作用下处理纳米载银无机抗菌剂粒子,分散制得PP/抗菌剂、PET/抗菌剂、PA/抗菌剂等复合树脂,然后经熔融纺丝工艺加工成抗菌纤维。研究表明,将经过表面处理的纳米抗菌剂粒子通过双螺杆挤出机熔融混炼,在聚合物中可以达到纳米尺度分散,获得了具有良好综合性能的纳米抗菌纤维,对大肠杆菌、金黄色葡萄球菌的抗菌率达到95%以上(美国AATCC-100标准)。  


    机械共混:将偶联剂稀释后与碳纳米管混合,再与超高分子量聚乙烯(UHMWPE)混合放入三头研磨机中研磨两小时以上。将研磨混合物放入模具,热压,制得功能型纳米复合材料。  


    聚合法:利用纳米SiO2粒子填充(Poly(HEMA))制备了纳米复合材料。纳米SiO2粒子首先被羟乙基甲基丙烯酸(HEMA)功能化,然后与HEMA单体在悬浮体系中聚合。还有利用SiO2胶体表面带酸性,加入碱性单体4-乙烯基吡咯进行自由基聚合制得包覆型纳米复合材料。