1) hydrothermal method
水热反应法
1.
Eu3+ or Gd3+ doped P-SiO2 and two ions co-doped P-SiO2 were synthesized by hydrothermal method.
通过水热反应法,获得了单掺和双掺Eu3+,Gd3+的多孔二氧化硅组装体,研究了掺杂体系的光谱特性,观察到Gd3+→Eu3+的能量传递。
2) hydrothermal reaction
水热反应
1.
A two-fold penetration coordination polymer [Cu(bpy)(OH)]n (1) (bpy=4,4'-bipyridyl) has been synthesized through hydrothermal reaction and structurally characterized by single crystal X-ray diffraction method.
利用水热反应,合成了一个具有二重穿插结构的一价铜配位聚合物[Cu(bpy)(OH)]n(1)(bpy=4,4'-联吡啶),并利用元素分析,X射线单晶衍射,红外光谱以及热重分析等手段对标题化合物进行了表征。
2.
Ferric inorganic polyeation was prepared from the materials of ferric chloride and sodium hydroxide which was mixed by difference proportion,thenα-Fe_2O_3 was synthesized using ferric inorganic polycation as precursor by hydrothermal reaction.
以三氯化铁和氢氧化钠为原料,按照不同的比例混合进行反应,得到铁的无机多聚离子,并采用水热反应合成了α-Fe_2O_3。
3.
Gypsum was used as raw material to prepare porous hydroxyapatite with hierachical structure by hydrothermal reaction.
使用石膏作为原料,通过水热反应得到具有特殊结构的多孔羟基磷灰石。
3) polymerization under hot water
热水反应
4) hydration reaction
水化热反应
5) hydrothermal reactor
水热反应器
6) reactive hot pressing
反应热压法
1.
Al_2O_3/NiCrAl composites and functional gradient materials fabricated by reactive hot pressing;
反应热压法制备Al_2O_3/NiCrAl复合材料及功能梯度材料
补充资料：晶体生长水热法
分子式：
CAS号：
性质： 在高温、高压水溶液中进行化学合成的一种方法。水热法不仅可以用于制备分子筛类的化合物，而且可以用来生长无机固体材料晶体。水的临界温度和压力分别为374℃和22MPa。在高温和高压下，水的离子积很大；例如在600℃和202.65MPa时，水的离子积是常温常压时的105倍。这意味着许多在通常条件下不溶于水的物质，在高温高压下可以溶于水。如果使体系产生一定的温度梯度，由于在不同温度下材料的溶解度不同，使材料晶体结晶出来。水热法生长晶体要在耐高压和高温的反应釜中进行。工业上应用水热法生长大尺寸的石英晶体。在生长晶体时，常在水中加入一定量的碱或酸，调节溶液的酸度，以调整材料在水中的溶解度。
CAS号：
性质： 在高温、高压水溶液中进行化学合成的一种方法。水热法不仅可以用于制备分子筛类的化合物，而且可以用来生长无机固体材料晶体。水的临界温度和压力分别为374℃和22MPa。在高温和高压下，水的离子积很大；例如在600℃和202.65MPa时，水的离子积是常温常压时的105倍。这意味着许多在通常条件下不溶于水的物质，在高温高压下可以溶于水。如果使体系产生一定的温度梯度，由于在不同温度下材料的溶解度不同，使材料晶体结晶出来。水热法生长晶体要在耐高压和高温的反应釜中进行。工业上应用水热法生长大尺寸的石英晶体。在生长晶体时，常在水中加入一定量的碱或酸，调节溶液的酸度，以调整材料在水中的溶解度。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。