1) Ni-S alloy
Ni-S合金
1.
Dependences of sulfur content during electro-deposition of Ni-S alloys;
电沉积Ni-S合金硫含量的影响因素
2.
Combining the development status of Ni-S alloy electrode used in alkaline water electrolysis at home and abroad,this paper has deeply researched and analyzed several key factors in preparation of Ni-S alloy electrode from the matrix material,pre-plating treatment,plating solution formulations,process parameters,after the plating treatment,additive elements and so on.
本文结合碱性水电解用Ni-S合金电极在国内外的发展现状,选择了从基体材料、镀前处理、镀液配方、工艺参数、镀后处理、添加元素等方面深入研究并分析了制备Ni-S合金电极的几个关键因素。
2) Ni-S-Co alloy
Ni-S-Co合金
1.
Preparation and electrochemical properties of amorphous Ni-S-Co alloy in alkaline medium;
非晶态Ni-S-Co合金的制备和电化学性能
3) Ni-Cr-S alloy
Ni-Cr-S合金
4) Ni-Ce-S alloy
Ni-Ce-S合金
5) amorphous Ni-S alloy
非晶态Ni-S合金
6) Ni-P-S alloy electrode
Ni-P-S合金电极
1.
On the basis of Ni-S alloy electrode made by electrodeposition method, Ni-P-S alloy electrode was obtained by adding sodium hypophosphite monohydrate into the bath.
在电沉积法制备Ni-S合金电极的基础上,向镀液中添加次亚磷酸钠制备了Ni-P-S合金电极。
补充资料：Ni3Al基金属间化合物高温合金
Ni3Al基金属间化合物高温合金
Ni_(3)Al-base intermetallic compound superalloy
N一3AIJ一J旧shuJ一an huahewu goowen heJ一nNi3AI基金属间化合物高温合金(Ni3AI一baseintermetallie eompound superalloy)以Ni3AI相为基体的金属间化合物高温合金。Ni3AI作为高温合金材料中的强化相口)早已被人们所熟知。单晶Ni3AI有较好的室温塑性和加工性，但多晶Ni3AI在室温的塑性儿乎为零。1979年，日本和泉修等发现，添加微量硼可使Ni3AI韧化。硼强烈地偏聚于晶界，从而提高晶界的结合强度并使晶界区无序化，因此提高了晶界区塑性变形能力，使Ni3AI的室温拉伸伸长率可达50%以上。纯净N珠AI的室温、高温强度偏低，与高温合金相比需要进一步提高。固溶强化(见高温合金固溶强化)是提高强度的一条有效途径。Ni3AI可以固溶很多元素，其中以错和铅的强化效果最显著。美国橡树岭国家试验室已发展了一系列含铬、错、错等元素的Ni3AI基金属间化合物高温合金，具有良好的强度、塑性和高温抗氧化性。中国也对Ni3AI基合金进行了深入研究，并添加微量镁显著改善了热加工塑性。Ni3AI基合金可能是最先在工业上得到使用的金属间化合物高温合金之一，已制成各种部件在试用，如汽轮机和柴油机的耐热部件、高温模具、加热元件以及航空用的紧固件等。 〔邹敦叙)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条