In this paper, the influences of specimen thickness and the size of crystal grain on mechanical properties of micro specimen of T2 copper foil are studied, the thickness of 100μm, 80μm and 60μm were selected with the heat treatment temperature of 400℃, 500℃, 600℃and 700℃, and the tensile speed is 0.
本文通过拉伸实验研究了T2紫铜箔微小试样的厚度和晶粒尺寸对力学性能的影响规律,选取的箔材厚度分别为100μm、80μm、60μm和40μm,热处理温度分别为400℃、500℃、600℃和700℃,拉伸速度为0。
3) T2 copper plank
T2紫铜板材
1.
T2 copper plank after anneal is used as testing material.
以380℃×40min退火态的T2紫铜板材为研究对象, 板材按C路径6道次的连续剪切变形后,经分析表明:连续剪切变形后的板材的显微组织明显得到细化,并且呈现出剪切流线形态;变形后的板材的抗拉强度由退火态的210MPa提高到330MPa;硬度从65HV1提高到120HV1。
4) T_2 pure copper strip
T2纯铜带
5) T2 copper
T2纯铜
1.
Two sequences of tension-fatigue and fatigue-tension were performed on T2 copper and brass H62 sheet.
本文以T2纯铜和H62黄铜为研究对象，进行拉伸—疲劳和疲劳—拉伸两种接续加载，两接续加载轴之间夹角Φ选取两个典型值(0°和45°)。
6) 10#steel
10#钢
补充资料：10,10'-oxybis-10H-Phenoxarsine
分子式：C24H16As2O3
分子量：502.2318
CAS号：58-36-6
性质：暂无
制备方法：暂无
用途：暂无
分子量：502.2318
CAS号：58-36-6
性质：暂无
制备方法：暂无
用途：暂无
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条