1) modified composite Portland cement
改性硅酸盐复合水泥
1.
To explain the mechanism of improving early strength of modified composite Portland cement, changing the content of gypsum, phosphoaluminate cement, and some additives, with orthogonal experience, and XRD, SEM, pore structure analysis etc.
通过设计正交试验探索掺磷铝酸盐水泥的改性硅酸盐复合水泥的力学性能,从石膏、磷铝酸盐水泥熟料、外加剂等因素调控,以改性后的硅酸盐复合水泥水化浆体的早期抗压强度为主要指标确定最佳方案,并与未改性的硅酸盐水泥强度作对比,并通过数据分析及XRD、SEM、孔结构分析等现代测试手段,解释改性硅酸盐复合水泥早期力学性能得以改善的机理。
2) modified portland cement
改性硅酸盐水泥
1.
The property change of modified Portland cement(alite sulphate aluminium cement) mixed with different type and content of admixture were studied,and also the effect of fineness and content of gypsum on cement properties as well,The mechanism of these changes was discussed by means of XRD analysis.
研究了不同混合材种类及掺量的改性硅酸盐水泥(即阿利特硫铝酸盐水泥)性能变化,以及水泥细度、石膏掺量等对水泥性能的影响,并借助XRD等测试技术对其机理进行探讨。
3) composite portland cement
复合硅酸盐水泥
1.
Study of production of high performance composite Portland cement for road with finely ground fly ash and steel slag;
利用超细粉煤灰及钢渣配制用于道路的复合硅酸盐水泥的试验研究
2.
It is considered that the porous silicon rock powder is a good natural active mixing material and is able to make mixing material portland cement or composite portland cement.
认为多孔硅质岩矿粉是一种良好的天然活性混合材料，可用于制作掺混合材料的硅酸盐水泥或复合硅酸盐水泥。
4) Compound Portland cement
复合硅酸盐水泥
1.
S or compound Portland cement with P·I clinker or P.
研究了水淬矿渣的特性，检测了不同细度、掺量的矿渣微粉与Ｐ·Ⅰ熟料或Ｐ·Ｏ配制的Ｐ·Ｓ或复合硅酸盐水泥的性质。
5) Complex Portland cement
复合道路硅酸盐水泥
6) modified portland cement
改良硅酸盐水泥
补充资料：抗硅酸盐水泥
分子式：
CAS号：
性质：以适当成分的生料，烧至部分熔融，而得到的硅酸钙为主要矿物组成的熟料，加入适量石膏，磨细制成的水硬性胶凝材料。具有抗硫酸盐侵蚀的特点。熟料中硅酸三钙含量不大于50％，铝酸三钙不大于5％，铝酸三钙及铁铝酸四钙含量不大于22％。适用于受硫酸盐侵蚀、冻融和干湿作用的海港、水利、地下、隧涵、引水、道路和桥梁基础等工程。
CAS号：
性质：以适当成分的生料，烧至部分熔融，而得到的硅酸钙为主要矿物组成的熟料，加入适量石膏，磨细制成的水硬性胶凝材料。具有抗硫酸盐侵蚀的特点。熟料中硅酸三钙含量不大于50％，铝酸三钙不大于5％，铝酸三钙及铁铝酸四钙含量不大于22％。适用于受硫酸盐侵蚀、冻融和干湿作用的海港、水利、地下、隧涵、引水、道路和桥梁基础等工程。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。