1) high C_3S cement system
高C_3S水泥
1.
Mechanics and drying shrinkage properties of high C_3S cement system;
高C_3S水泥系统的力学性能及干缩性能
4) high C3S
高C_3S
1.
The traditional 50-60% C3S content limit of clinker was surpassed by the named high C3S clinker with about 70% C3S.
高C_3S水泥熟料突破了传统硅酸盐水泥熟料的组成局限,要求熟料中C_3S含量由50～60%提高到70%左右。
5) tricalcium silicate
C_3S
1.
Using isothermal sintering,formation kinetics of tricalcium silicate with different content of SO_3(0%,1%,2%,3%,3.
5%,5%)的C_3S矿物形成过程从动力学角度进行了系统探讨。
6) high alumina cement
高铝水泥
1.
Limestone powder was used as a filler to modify high alumina cement.
以CaCO3微粉作改性剂对高铝水泥进行改性。
2.
In the high alumina cement, dicalcium aluminate silicate is transformed into Q phase.
将高铝水泥中的惰性成分硅铝酸二钙(C2AS)转化为水化活性良好的Q相,组成Q相铝酸一钙(CA)七铝酸十二钙(C12A7)高铝水泥系统,对此系统的烧成条件进行研究。
3.
Using grog,haydite as aggregate,high alumina cement as binder,and using compound early strength agent,the high strength haydite castable material produced successfully This castable material has the characters of early strengthened,good heat preservation,good resistance to wear,small volume density and good constraction property,etc This castable material has good utilization effect in productio
以焦宝石、陶粒为骨料 ,高铝水泥作结合剂及采用复合早强剂 ,研制成功高强陶粒浇注料。
补充资料：高分子纤维增强水泥复合材料
高分子纤维增强水泥复合材料
polymer fibre reinforced cementitious composites
高分子纤维增强水泥复合材料Polymer fibrereinforeed cementitious composites以高分子合成纤维(聚酞胺、聚烯烃、聚醋类等)增强硅酸盐水泥构成的复合材料。 合成纤维的主要特点是密度小(0 .9一1.59/cma)，抗拉强度高(500一3500MPa)，弹性模量低(10一100GPa)，断裂延伸率大(3一12%)，吸水率小，耐磨性好，耐热性差。其中尼龙、聚丙烯、聚乙烯、芳族聚酞亚胺等纤维因耐碱性较好而常用作水泥基复合材料的增强纤维。纤维的弹性模量大于基体的弹性模量(巧一3OGPa)才有增强作用，一般合成纤维难于满足。已研制高模量纤维，弹性模量可高达150GPa。若用低弹模纤维则仅提高复合材料的变形能力、韧性和抗冲能力，对裂缝控制亦可改善。不同品种纤维性能各异，同时掺加两种以上纤维，可相互取长补短，其性能优于掺单一纤维者。常用抄取法、流浆法以短切纤维加入水泥浆，也可用膜裂纤维网或树脂胶结高强度长纤维扎成筋棒加入。后者造价很高，仅用作耐腐蚀、防电磁、有特殊要求的混凝土。掺纤维的同时掺入硅灰、超塑化剂，或采用上抛式搅拌机有助于纤维在浆体中分散均匀。某些纤维适合进行压蒸养护，以提高其抗弯强度，并减少收缩率。目前纤维掺入体积分数约为0.5一6.0%。当用高模量纤维时，抗弯强度可达10一30MPa，主要用于代替石棉制品。(陈志源)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。