1) Dielectric relaxation
介电松弛
1.
An extremely large dielectric relaxation called αH which has a relaxation strength as high as 25300 was observed in nylon 11.
研究了尼龙１１在高温下的介电松弛温度谱和频率谱，发现了１个新的超强介电松弛峰——αＨ松弛峰，其松弛强度Δε可达２５３００，松弛活化能ΔＥ为８９。
2.
5)/HeFP(5)in the range of-120-40℃,10~(-2)—10~4 Hz were measured bythe improved dielectric relaxation spectrometer.
用改进的介电松弛谱仪(精度 2‰)测定了 VDF(52)/TrFE(48)和VDF(47。
3.
The behavior of dielectric relaxation indicates that α— relaxation of copolymer VF_2(95)/VF(5) disappears, the relaxation time prolonges, the relaxation strength of amorphous region decreases, T_(?) increases by 3℃ and the activation energy o.
利用改进了的仪器对聚偏氟乙烯(PVDF)及偏氟乙烯(95)/氟乙烯(5)共聚物进行了介电性质研究,发现由于5%氟乙烯存在,致使共聚物较之PVDF,其链结构规整性降低,α型介电松弛消失,非晶松弛强度减弱,T_(?)升高3℃,局域松弛活化能增大5。
2) Dielectic Spectra
介电松弛谱
3) relaxation,spectra of dielectric
介电常数的松弛光谱
4) cable slack
电缆松弛
5) dielectric relaxation
介电弛豫
1.
Study on dielectric relaxation of Ba(Ti_(0.91)Zr_(0.09))O_3 ceramics;
Ba(Ti_(0.91)Zr_(0.09_)O_3陶瓷介电弛豫现象的研究
2.
The low-frequency dielectric relaxation in Pt/Ba_(0.8)Sr_(0.2)TiO_3/Pt thin film capacitors post annealed at low temperatures in oxygen ambient;
氧气氛低温退火Pt/Ba_(0.8)Sr_(0.2)TiO_3Pt引起的低频介电弛豫效应
3.
Thermal behaviours of dielectric relaxation of polymers;
聚合物介电弛豫的温度特性
补充资料：介电松弛
分子式：
CAS号：
性质：又称介电弛豫。电介质在外电场作用(或移去)后，从瞬时建立的极化状态达到新的极化平衡态的过程。电介质极化趋于稳态的时间称为松弛时间。松弛时间与极化机制密切相关，是造成介质材料存在介质损耗的原因之一。通过研究高分子材料的介电松弛，不仅可以获得其松弛时间，而且因为在实际测量中，往往要测量介电谱，从而通过数学处理后可获得分子间相互作用的状态，根据高频侧α值与低频侧α值的差确定曲线宽度，曲线宽表示分子间相互作用大，曲线窄表示分子间相互作用小。
CAS号：
性质：又称介电弛豫。电介质在外电场作用(或移去)后，从瞬时建立的极化状态达到新的极化平衡态的过程。电介质极化趋于稳态的时间称为松弛时间。松弛时间与极化机制密切相关，是造成介质材料存在介质损耗的原因之一。通过研究高分子材料的介电松弛，不仅可以获得其松弛时间，而且因为在实际测量中，往往要测量介电谱，从而通过数学处理后可获得分子间相互作用的状态，根据高频侧α值与低频侧α值的差确定曲线宽度，曲线宽表示分子间相互作用大，曲线窄表示分子间相互作用小。