1) Ni/MgO-Al_2O_3
Ni/MgO-Al2O3
1.
The effects of calcination temperature on the properties of Ni/MgO-Al_2O_3 were studied by the means of XRD, TPR, BET,TG and catalytic performance evaluation.
采用TPR、BET、XRD、TG及反应性能评价等研究方法,考察了焙烧温度对甲烷催化部分氧化制合成气Ni/MgO-Al2O3催化剂结构和性能的影响。
2) Ni/MgO-Al2O3 catalyst
Ni/MgO-Al2O3催化剂
1.
The effects of CeO2 and/or CaO as promoters on the physico-chemical properties and the catalytic performance over Ni/MgO-Al2O3 catalyst for partial oxidation of methane to syngas were studied by means of BET,XRD,H2-TPR,TEM and reaction activity evaluation.
采用BET、H2-TPR、XRD、TEM和活性评价等表征手段,考察了CeO2、CaO助剂对Ni/MgO-Al2O3催化剂物化性质和甲烷部分氧化制合成气反应性能的影响。
3) Ni/MgO/Al2O3 catalyst
Ni/MgO/Al2O3催化剂
4) MgO/Al 2O 3
MgO/Al2O3
5) Ni-Al_(2)O_(3)
Ni-Al2O3
6) MgO-Al2O3-SiO2
MgO-Al2O3-SiO2系
1.
LTCC precursor of MgO-Al2O3-SiO2 system prepared by sol-gel method was calcined at 700℃ for 2h to obtain the LTCC substrate powder.
采用溶胶-凝胶法制备MgO-Al2O3-SiO2系低温共烧陶瓷(LTCC)基板粉料的先驱体,经700℃焙烧制得LTCC基板粉体,在850、900℃下烧结成LTCC基板样品。
补充资料：Ni-Al microwave ferrite
分子式：Ni-Al
CAS号：
性质：又称镍-铝微波铁氧体。在镍旋磁铁氧体基础上，用三价铝离子置换一部分三价铁离子形成的镍-铝旋磁铁氧体。化学式为NiAlxFe2-xO4。当Alx的x值达约0.7%，磁性出现反常现象，这时材料已无实用值。按铝含量而分为0.1≤x≤0.4和0.7≤x≤1.0两类旋磁铁氧体。饱和磁化强度0.035～0.145T，随铝量换量的增加而降低。居里温度155～440℃。铁磁共振线宽18.0～44.0kA/m(9kHz)。介电常数8.2～9.5。介质损耗角正切值（3～50）×10-4。采用电子陶瓷工艺，热压烧结或氮气氛烧结。适于制作高功率器件。
CAS号：
性质：又称镍-铝微波铁氧体。在镍旋磁铁氧体基础上，用三价铝离子置换一部分三价铁离子形成的镍-铝旋磁铁氧体。化学式为NiAlxFe2-xO4。当Alx的x值达约0.7%，磁性出现反常现象，这时材料已无实用值。按铝含量而分为0.1≤x≤0.4和0.7≤x≤1.0两类旋磁铁氧体。饱和磁化强度0.035～0.145T，随铝量换量的增加而降低。居里温度155～440℃。铁磁共振线宽18.0～44.0kA/m(9kHz)。介电常数8.2～9.5。介质损耗角正切值（3～50）×10-4。采用电子陶瓷工艺，热压烧结或氮气氛烧结。适于制作高功率器件。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。