1)  steel cooling wall
钢冷却壁
2)  cast steel cooling stave
铸钢冷却壁
1.
The thermal test system of cooling stave was designed and established to put up the industrial experiment of the heat transfer for the cast steel cooling stave and ductile iron cooling stave.
设计并建造了冷却壁热态试验系统,对铸钢冷却壁和球墨铸铁冷却壁的换热效果进行了工业模拟试验。
2.
The temperature and thermal stress fields of cast steel cooling stave are calculated by finite element method software ANSYS in blast furnace at Maanshan Iron and Steel Co.
采用通用有限元软件ANSYS计算了300 m3高炉铸钢冷却壁的温度场和应力场,数值分析铸钢冷却壁冷却水管内径、间距、壁体厚度、镶砖厚度以及冷却水流速对冷却壁热面最高温度和热应力的影响。
3.
Three parts (84 pieces) of cast steel cooling staves are installed centrally during the intermediate relining of No.
济钢 4#高炉中修集中安装三段 (84块 )铸钢冷却壁后 ,因铸钢冷却壁冷却强度大 ,易造成炉墙结厚 ,通过采用控制合适的水流量及水温差、相应的装料制度、热制度、送风制度及上下调剂的操作制度 ,达到了高炉高效顺行又长寿的目
3)  copper-steel cooling stave
铜钢复合冷却壁
4)  cooling wall
冷却壁
1.
Failure analysis and prevention for the damaged cooling wall of No.4 BF at Guangsteel;
广钢4号高炉冷却壁破损原因及维护措施
2.
Leak detecting for soft water closed circulation system and solution on making water of cooling wall are also introduced.
分析高炉软水密闭系统本体检漏、冷却壁漏水处理方法。
3.
6 section cooling wall tube root of blast furnace bosh were analyzed from three aspect cooling water of the blast furnace,body of the cooling wall and operation of the blast furnace,and according measures were decided to reduce and eliminate the breakage.
从高炉冷却水、冷却壁本体、高炉操作等三个方面对高炉炉腹第五、六段冷却壁管根破损的原因进行分析,并制定相应的应对措施来消除或减少其对高炉的影响。
5)  copper cooling stave
铜冷却壁
1.
Model for inner proffie control of furnace wall lined with copper cooling stave based on the inverse problems in heat transmission;
铜冷却壁炉墙内型管理传热学反问题模型
2.
Study on the hot characteristics of hot and cold sides of the copper cooling stave with circular channels;
圆孔型铜冷却壁冷面及热面热态特性研究
3.
Adopting copper cooling stave to prolong BF campaign;
采用铜冷却壁延长高炉炉体寿命
6)  stave [英][steɪv]  [美][stev]
冷却壁
1.
The calculation models of the heat transfer coefficient between the blast furnace gas flow and the heat surface of stave are established based on the substitution method of boundary condition.
基于边界条件替代法建立了高炉冷却壁热表面与炉气间的传热系数计算模型。
2.
4 blast furnace was considerably deteriorated, with its shaft's stave seriously damaged, the temperature of the cooling water in the furnace hearth's stave abnormally increased, the furnace bottom's temperature reaching an alarming level, and the furnace shell cracked and deformed in a number of locations.
韶钢4#高炉第一代炉役后期,炉身冷却壁大量损坏,炉缸部分冷却壁水温差超高,炉底、炉基温度达到安全警戒线,炉壳多处开裂变形,依靠外部打水维持生产的情况下,通过采取强化管理、加强高炉操作、炉体修补等措施,保证了高炉按计划安全停炉并创下投产以来的最好生产指标。
补充资料:45钢和40Cr钢调质的热处理工艺
45钢40Cr钢调质                         
    调质是淬火加高温回火的双重热处理,其目的是使工件具有良好的综合机械性能。
    调质钢有碳素调质钢和合金调质钢二大类,不管是碳钢还是合金钢,其含碳量控制比较严格。如果含碳量过高,调质后工件的强度虽高,但韧性不够,如含碳量过低,韧性提高而强度不足。为使调质件得到好的综合性能,一般含碳量控制在0.30~0.50%。

    调质淬火时,要求工件整个截面淬透,使工件得到以细针状淬火马氏体为主的显微组织。通过高温回火,得到以均匀回火索氏体为主的显微组织。小型工厂不可能每炉搞金相分析,一般只作硬度测试,这就是说,淬火后的硬度必须达到该材料的淬火硬度,回火后硬度按图要求来检查。 

工件调质处理的操作,必须严格按工艺文件执行,我们只是对操作过程中如何实施工艺提些看法。


   1、 45钢的调质
   45钢是中碳结构钢,冷热加工性能都不错,机械性能较好,且价格低、来源广,所以应用广泛。它的最大弱点是淬透性低,截面尺寸大和要求比较高的工件不宜采用。


   45钢淬火温度在A3+(30~50) ℃,在实际操作中,一般是取上限的。偏高的淬火温度可以使工件加热速度加快,表面氧化减少,且能提高工效。为使工件的奥氏体均匀化,就需要足够的保温时间。如果实际装炉量大,就需适当延长保温时间。不然,可能会出现因加热不均匀造成硬度不足的现象。但保温时间过长,也会也出现晶粒粗大,氧化脱碳严重的弊病,影响淬火质量。我们认为,如装炉量大于工艺文件的规定,加热保温时间需延长1/5。


   因为45钢淬透性低,故应采用冷却速度大的10%盐水溶液。工件入水后,应该淬透,但不是冷透,如果工件在盐水中冷透,就有可能使工件开裂,这是因为当工件冷却到180℃左右时,奥氏体迅速转变为马氏体造成过大的组织应力所致。因此,当淬火工件快冷到该温度区域,就应采取缓冷的方法。由于出水温度难以掌握,须凭经验操作,当水中的工件抖动停止,即可出水空冷(如能油冷更好)。另外,工件入水宜动不宜静,应按照工件的几何形状,作规则运动。静止的冷却介质加上静止的工件,导致硬度不均匀,应力不均匀而使工件变形大,甚至开裂。


说明:补充资料仅用于学习参考,请勿用于其它任何用途。