1) Zn-Al-Mn alloy coating
锌铝锰镀层
2) Al-Zn coating
铝锌镀层
3) Zn and Mn double-coating
锌锰双镀层
1.
Mass and thickness of coating for Zn and Mn double-coating steel wire are determined by FAAS,coating immersion adopt HCl and SbCl 3,contents of Zn and Mn can be determined in the same solution,the rate of recovery of Zn 2+ is 98.
用原子吸收分光光度法测定钢丝锌锰双镀层的镀层质量及厚度 ,镀层浸取液采用盐酸加SbCl3 ,在同一份溶液中可分别测定锌量和锰量 ,Zn2 +的回收率可达 98。
4) 5%Al-Zn alloy coating
5%铝-锌镀层
5) 55%Al-Zn coating
55%铝-锌镀层
1.
The results indicated that the 55%Al-Zn coating is superior to conventionally galvanized coating and 5%Al-Zn coating in anticorrosivity when its specimens were immersed in seawater because of its low corrosion current density and protective corrosion products.
结果表明,由于腐蚀电流密度小,腐蚀产物具有保护性,55%铝-锌镀层在全浸区的耐蚀性能比镀锌层和5%铝-锌镀层好;由于保护性锌的腐蚀产物被滞留在富铝的枝晶网络中,充分的充气条件又促进了镀层富铝相的钝化,镀层腐蚀的传质过程受到明显抑制,所以55%铝-锌镀层在潮差区和飞溅区的耐蚀性能显著优于全浸区,是全浸区的2到3倍;值得注意的是,镀层在全浸区出现较严重的局部腐蚀。
6) Zn-Mn alloy deposit
锌锰合金镀层
补充资料：铝-锌系铸造铝合金
分子式：
CAS号：
性质：以锌为主要合金元素的铸造铝合金，是最早获得工业应用的铝合金之一。在工业中应用的Al-Zn系铸造铝合金成分是5％～14％Zn，2％～3％Cu，6％～8％ Si，0.1％～0.7％Mg，并含有少量其他元素。Al-Zn-Cu合金强度较高、切削加工性能和焊接性能良好，但铸造性能和抗腐蚀性能差。Al-Zn-Mg合金具有良好的力学性能和抗腐蚀性能，可以在淬火时效状态下使用，具有更高的强度。另外该合金的熔化温度较高，但其铸造工艺性能较差。Al-Zn-Si合金具有较高的力学性能和良好的铸造性能，广泛用于砂型、金属型和压力铸造。
CAS号：
性质：以锌为主要合金元素的铸造铝合金，是最早获得工业应用的铝合金之一。在工业中应用的Al-Zn系铸造铝合金成分是5％～14％Zn，2％～3％Cu，6％～8％ Si，0.1％～0.7％Mg，并含有少量其他元素。Al-Zn-Cu合金强度较高、切削加工性能和焊接性能良好，但铸造性能和抗腐蚀性能差。Al-Zn-Mg合金具有良好的力学性能和抗腐蚀性能，可以在淬火时效状态下使用，具有更高的强度。另外该合金的熔化温度较高，但其铸造工艺性能较差。Al-Zn-Si合金具有较高的力学性能和良好的铸造性能，广泛用于砂型、金属型和压力铸造。