1) high temperature small fatigue crack
高温疲劳小裂纹
2) high temperature fatigue cracks
高温疲劳裂纹
1.
The method of reducing load and observing by eyes were used to test the threshold of load and propagation rate of high temperature fatigue cracks in the center crack specimens which were made of alloy based Nickel.
采用降载法和目测法对高温镍基合金的中心裂纹试样进行了高温疲劳裂纹的门槛值试验和扩展速率试验,并分析讨论了高温下疲劳裂纹的扩展规律及其影响因素。
3) Fatigue Small Crack
疲劳小裂纹
1.
Study on Fatigue Small Crack Propagation Behavior in TA6V Titanium Alloy;
TA6V钛合金疲劳小裂纹扩展行为研究
4) fatigue crack
疲劳裂纹
1.
Research on fatigue crack growth behaviors of 16MnR steel at elevated temperature.;
16MnR钢高温疲劳裂纹扩展行为试验研究
2.
Effects of residual stress on the delay of fatigue crack initiation in the mixed-mode stress field for aluminum alloys;
残余应力对铝合金在混和应力场中疲劳裂纹的延迟作用
3.
Application of neural networks to the evolution of fatigue cracks;
应用神经网络的疲劳裂纹演化规律的描述
6) endurance crack
疲劳裂纹
1.
Using ultrasonic to inspect endurance crack in collar thread;
钻铤螺纹疲劳裂纹的超声波检测
2.
The article focuses on the aspects as follows: the analysis for reasons of endurance crack, the chemical composition analysis of roller material, the selection of base metal and electrodes for repairing, the determination of welding parameters, the pre heat and post heat trea.
介绍了大型卷板机主动辊断裂后修复的技术过程及经济性分析 ,疲劳裂纹形成的原因 ;辊子材料材质的化学分析 ;补焊材料材质的确定 ;焊接材料的选择 ;合理的焊接工艺参数的确定 ;焊前预热及焊后热处理方法 ;焊后超声波检查及其它检验方法 ;焊接修复的经济性分析 。
3.
This paper gives all-round analysis to the endurance crack in the hull structure and tells the main causes for such endurance crack for reference.
有些船舶在不同的船龄阶段 ,在船体结构上出现疲劳裂纹 ,特别是在船底、舷侧纵骨中较为突出。
补充资料：疲劳裂纹生长
分子式：
CAS号：
性质：材料在连续交变应力作用下，会在其表面逐渐生成裂纹，并随着作用时间而逐渐向纵深发展，使裂纹扩展，试件的力学性能下降，最终导致完全断裂。应该指出，有些材料耐初始裂纹生长的性能很好，但一旦生成却发展很快。而另一些材料就正好相反。所以对疲劳裂纹的生成和发展是疲劳试验中最关心的性状之一。