1) critical inclusion size
临界夹杂物尺寸
1.
The critical inclusion sizes (CIS) of some steels with given matrix hardness or tensile strength and surface roughness under high cycle fatigue condition were estimated mainly on the basis of Murakami's theory, i.
依据Murakami的“夹杂物等效投影面积模型”估算了在高周疲劳条件下一定硬度(或强度)高强钢的“临界夹杂物尺寸:。
2) inclusion size
夹杂物尺寸
1.
Further investigation revealed that this difference is mainly caused by the difference in inclusion size.
结果表明,虽然实验料的氧含量相同,但由于钢中夹杂物尺寸的差异,使其高周疲劳性能存在明显差异。
2.
The mechanism of ultra high cycles fatigue fracture of high strength steel,especially the effect of inclusion size on fatigue life,were investigated.
为提高工程结构用钢的使用寿命,研究了高强度廉价耐候钢,特别是Mn-Cu细-晶,PR-E-超细晶的协同作用和超低碳贝氏体组织对钢耐蚀性的影响;为提高机械制造用钢的使用寿命,研究了高强度钢的超高周疲劳断裂机制,特别是夹杂物尺寸对钢疲劳性能的影响;为提高合金结构钢的质量研究了微米级夹杂物的形成理论和控制技术。
3) size of maximum inclusion
最大夹杂物尺寸
4) inclusion size distribution
夹杂物尺寸分布
5) large-dimension inclusion
大尺寸夹杂物
6) critical dimension
临界尺寸
1.
The model was analyzed and established,then the formula of critical dimension was got,which was related to the temperature distribution of heater tip.
根据传热学建立了脉冲热压焊的焊咀温度分布模型,对该模型进行分析、计算,得到了焊咀端部温度分布是否分布均匀的临界尺寸公式。
2.
The results showed that the critical dimension for Poplar increased wh.
02 MPa的真空干燥条件下,通过未封面与侧面封闭试件的对比试验,对杨木真空干燥临界尺寸进行了研究。
补充资料：临界尺寸（criticalsize）
临界尺寸（criticalsize）
见“超导体小样品”。它也是超导电性尺寸效应物性呈现的标志。由GL理论所得的若干结果如下：
厚为2d的超导薄膜，磁场平行于膜面：
`d_K=sqrt5\delta_0//2`
半径为r的超导球体：
$r_K=sqrt{21}\delta_0//2$
纵向和横向磁场中半径为r的超导圆柱体均为：
$r_K=sqrt3\delta_0$
对于“长轴半径$a\gt\gt$短轴半径b”的超导椭球体，在纵向磁场中：
$L_K\equivb=sqrt{3//2}\delta_0$
在横向磁场中：
$L_K\equivsqrt{ab}=sqrt{7//\pi}\delta_0$
说明：补充资料仅用于学习参考，请勿用于其它任何用途。