1) Soudium 2-acrylamide-2-methyl-propyl sulfonic acid
2-丙烯酰胺基-2-甲基丙烷磺酸钠
2) 2-acrylamido-2-methylpropane sulfonic acid sodium salt
2-丙烯酰胺基-2-甲基丙磺酸钠
1.
The polysiloxane modified acrylates soap-free emulsion was obtained using water-soluble potassium persulfate/sodium bisulfite as redox initiation system and 2-acrylamido-2-methylpropane sulfonic acid sodium salt(AMPS)as surfmer.
以过硫酸钾/亚硫酸氢钠为氧化还原体系,合成了由表面活性单体2-丙烯酰胺基-2-甲基丙磺酸钠(AMPS)稳定的硅丙无皂乳液。
3) sodium 2-acrylamido-2-methylpropanesulfonate
2-丙烯酰胺基-2-甲基-丙磺酸钠
1.
Water soluble hydrophobic associative acrylamide-sodium 2-acrylamido-2-methylpropanesulfonate-perfluorohexylethyl methacrylate terpolymer containing fluorocarbon group were synthesized by emulsion copolymerization.
采用胶束聚合法制备了丙烯酰胺/2-丙烯酰胺基-2-甲基-丙磺酸钠/全氟己基乙基甲基丙烯酸酯三元含氟碳基团的水溶性疏水缔合共聚物,用傅里叶变换红外光谱对该共聚物的结构进行了表征,用热重分析研究了它的热稳定性。
4) 2-acrylamido-2-methylproanesulfonic acid
2-丙烯酰胺基-2-甲基丙烷磺酸
5) Acrylamido-2-methylpropanesulfuric Acid(AMPS)
2-丙烯酰胺基-2-甲基丙烷磺酸(AMPS)
6) 2-acrylamido-2-methyipropanesulfonate sodium
2-丙烯酰胺-2-甲基丙磺酸钠
补充资料：2-丙烯酰氨基-2-甲基丙烷磺酸
分子式：C7H13NO4S
分子量：207.250
CAS号：15214-89-8
性质：白色结晶。熔点195℃(分解)。溶于水，溶液呈酸性。溶于二甲酰胺，部分溶于甲醇，乙醇，难溶于丙酮。略有酸味。
制备方法：有一步法和两步法两种。一步法是将原料丙烯腈，异丁烯，发烟硫酸一起反应。两步法是在反应溶剂的存在下，先将异丁烯磺化，得到磺化中间体，然后在硫酸存在下与丙烯腈反应。一步法较经济。原料消耗定额：异丁烯300kg/t、丙烯腈290kg/t、发烟硫酸辣560kg/t。
用途：该品分子内有聚合性的乙烯基及亲水性的磺酸基，可与丙烯腈，丙烯酰胺等水溶性单体，苯乙烯，氯乙烯等非水溶性单体共聚。在聚合物中引进亲水性的磺酸基，使纤维、薄膜等具有吸湿性透水性及导电性。可用于造纸工业及废水处理。作涂料改性剂，纤维改性剂和医用聚合物等。
分子量：207.250
CAS号：15214-89-8
性质：白色结晶。熔点195℃(分解)。溶于水，溶液呈酸性。溶于二甲酰胺，部分溶于甲醇，乙醇，难溶于丙酮。略有酸味。
制备方法：有一步法和两步法两种。一步法是将原料丙烯腈，异丁烯，发烟硫酸一起反应。两步法是在反应溶剂的存在下，先将异丁烯磺化，得到磺化中间体，然后在硫酸存在下与丙烯腈反应。一步法较经济。原料消耗定额：异丁烯300kg/t、丙烯腈290kg/t、发烟硫酸辣560kg/t。
用途：该品分子内有聚合性的乙烯基及亲水性的磺酸基，可与丙烯腈，丙烯酰胺等水溶性单体，苯乙烯，氯乙烯等非水溶性单体共聚。在聚合物中引进亲水性的磺酸基，使纤维、薄膜等具有吸湿性透水性及导电性。可用于造纸工业及废水处理。作涂料改性剂，纤维改性剂和医用聚合物等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。