1) fatigue crack initiation and propagation
疲劳裂纹萌生及扩展
1.
SEM in situ observations for the effects of inclusions on the fatigue crack initiation and propagation behaviors of super strength steel indicate that the inclusion size and shape affect not only on the fatigue crack initiation location but also on the crack growth behavior.
采用扫描电镜原位观测了数微米大小夹杂物对超高强度钢疲劳裂纹萌生及扩展的影响,并用有限元法解释了夹杂物尺寸 和形状对疲劳裂纹萌生及初期扩展的影响程度,得到了超高强度钢低周疲劳裂纹萌生与扩展特性和夹杂物对疲劳破坏的关键尺寸的 估计值。
2) Fatigue crackle sprouting and its extending
疲劳裂纹的萌生及扩展
3) Thermal fatigue crack initiation and propagation
热疲劳裂纹的萌生与扩展
4) fatigue crack initiation
疲劳裂纹萌生
1.
Study on fatigue crack initiation and propagation of cast aluminum alloy A356;
A356铸造铝合金的疲劳裂纹萌生及短裂纹扩展研究
2.
Cyclic stress response behavior, fatigue crack initiation and propagation behavior and (corresponding) fracture characteristics of magnesium alloys under fatigue loading condition are summarized.
简要介绍了镁合金在疲劳加载条件下的循环应力响应行为、疲劳裂纹萌生与扩展行为以及疲劳断裂的微观特征,分析了镁合金的显微组织、冶金和表面状态等材料内在因素以及环境、温度等外部因素对镁合金的疲劳强度、疲劳寿命、疲劳裂纹扩展速率的影响规律,指出了机械抛光、喷丸处理、表面滚压等表面机械加工方法以及适当的热处理均可有效地提高镁合金的疲劳强度和疲劳寿命。
3.
It was found that the grain boundaries are the preferred sites for fatigue crack initiation in the fatigued bicrystals.
在滑移带撞击晶界的地方，特别是在几条粗滑移带共同撞击晶界的地方观察到许多疲劳微裂纹；并且发现与平行晶界双晶相比，垂直晶界双晶中极有利于疲劳裂纹沿晶界作早期扩展一种PSB－GB疲劳裂纹萌生机制可用来解释这些沿晶疲劳裂纹的形成。
5) fatigue crack propagation
疲劳裂纹扩展
1.
Effect of laser surface melting on fatigue crack propagation of eutectic aluminum silicon alloy;
激光表面熔凝处理对共晶铝硅合金疲劳裂纹扩展的影响
2.
Elastic-plastic fatigue crack propagation under combined torsion and tension;
扭转/拉伸复合载荷下的弹塑性疲劳裂纹扩展行为
3.
Influence of stress ratio R on threshold value △K_(th) of fatigue crack propagation for welded joints of 09CuPCrNi steel;
应力比R对09CuPCrNi钢焊接接头疲劳裂纹扩展门槛值△K_(th)的影响
6) fatigue crack growth
疲劳裂纹扩展
1.
Effect of welding residual stress on fatigue crack growth of the pressure vessel;
焊接残余应力对压力容器疲劳裂纹扩展的影响
2.
Cyclic plasticity and fatigue crack growth threshold;
循环塑性与疲劳裂纹扩展门槛值(英文)
3.
Engineering estimation method of low-cycle fatigue crack growth rate of the pressure vessel;
压力容器低周疲劳裂纹扩展率的工程计算方法
补充资料：裂纹失稳扩展
分子式：
CAS号：
性质：材料内部裂纹尖端的应力场强度因子达到或超过材料的断裂韧性之后发生的裂纹快速扩展。裂纹失稳扩展将导致材料迅速断裂。
CAS号：
性质：材料内部裂纹尖端的应力场强度因子达到或超过材料的断裂韧性之后发生的裂纹快速扩展。裂纹失稳扩展将导致材料迅速断裂。