1) antimony sulfide
硫化锑
1.
The problem of low sensitivity and difficult control due to applying lead tetraoxide-silicon delay compounds,antimony sulfide,as delayer to detonator with many half-second delay periods is solved.
研究解决了铅丹—硅系延期药用硫化锑作缓燃剂在高段半秒延期导爆管雷管中感度低、秒量不易控制的难题,产品的各项性能全部符合国家标准。
2.
The problem of low sensitivity and low precision of second quantity due to applying lead tetraoxide-silicon delay compounds,antimony sulfide as delayer in half-second delay detonator with shock-conducting tube is solved in this paper.
研究解决了铅丹-硅系列延期药用硫化锑作缓燃剂在高段半秒延期导爆管雷管中感度低、秒量精度不高的难题。
2) antimony sulphide
硫化锑
1.
This paper studies on the absorbing properties of the monolayer composites of epoxy filled with Sb_2S_3(Antimony sulphide), MnO_2(Manganese dioxide), and CB(carbon black), as well as the absorbing properties of the bilayer composites of Sb_2S_3/CB, MnO_2/CB and CB/CB respectively.
本论文首次对硫化锑、二氧化锰、炭粉分别填充环氧树脂所得单层复合材料和硫化锑／炭型双层复合材料、二氧化锰／炭型双层复合材料、炭／炭型双层复合材料的吸波性能进行了研究。
3) antimonous sulfide
硫化亚锑
1.
Two pharmaceutical carriers made of antimonous sulfide nanocolloids with different particale size distribution were prepared by using two different sources of sulfide.
采用两种不同的硫源 ,制备了两种不同粒径分布的药用载体——硫化亚锑纳米胶粒。
4) Antimony sulfuret
三硫化锑
1.
The volatization of Antimony sulfuret in argon atmosphere at different temperatures is investigated.
研究了三硫化锑在氩气中不同温度下的挥发情况,实验结果表明,温度一定时,挥发速率常数在一段时间内为一定值;温度越高,挥发速率常数越大。
5) Sb2S3 ores
硫化锑矿
补充资料：硫化锑
有三硫化二锑Sb2S3和五硫化二锑Sb2S5两种。天然的三硫化二锑矿称辉锑矿,一般为灰色、具有金属光泽的斜方晶体;晶格由(Sb2S3)∞链组成,链间以弱的结合形成层；相对密度4.64，熔点550℃,沸点约为1150℃。三硫化二锑在隔绝空气下强烈加热，可被蒸馏而不分解。三硫化二锑不溶于水，可溶于浓盐酸、氢氧化钠和硫化铵溶液。将硫化氢通入三价锑盐的微酸性溶液，得到的三硫化二锑沉淀为橙红色无定形粉末，在 250℃以上隔绝空气加热可转化为结晶型。三硫化二锑可用于制造颜料、焰火和火柴等。
五硫化二锑为橙红色粉末；相对密度4.12；不溶于水,可溶于浓盐酸、氢氧化钠和硫化铵溶液;在75℃时分解为三硫化二锑。将稀盐酸或稀硫酸与硫代锑酸盐（如Na3SbS4）作用,可制得五硫化二锑，可用作兽药，也用于树脂的加硫。
五硫化二锑为橙红色粉末；相对密度4.12；不溶于水,可溶于浓盐酸、氢氧化钠和硫化铵溶液;在75℃时分解为三硫化二锑。将稀盐酸或稀硫酸与硫代锑酸盐（如Na3SbS4）作用,可制得五硫化二锑，可用作兽药，也用于树脂的加硫。