1) Poly(ethylvinyl benzene-10-divinylbenzene)beads
聚苯乙烯-二乙烯苯微球
2) polydivinylbenzene microspheres
聚二乙烯苯微球
3) PST-DVB microsphere
聚苯乙烯-二乙烯基苯微球
4) micro-spherical poly-St-DVB resin
聚苯乙烯-二乙烯苯微球载体
5) poly(styrene-divinylbenzen)microsphere
苯乙烯-二乙烯苯共聚微球
6) polystyrene microspheres
聚苯乙烯微球
1.
Factors influencing size of polystyrene microspheres in dispersion polymerization;
分散聚合反应中影响聚苯乙烯微球粒径的因素
2.
Evaporation self-assembly method, which is used to assemble sub-micrometer polystyrene microspheres, is presented in this paper.
建立了一种组装亚微米级聚苯乙烯微球的方法,称作蒸发自组装法。
3.
Monodisperse polystyrene microspheres were prepared by dispersion polymerization in ethyl alcohol reaction media using polyvinylpyrrolidone (PVP) as steric stabilizer and 2,2-azobisizobutyronitrile (AIBN) as initiator in a suitable condition.
以聚乙烯基吡咯烷酮 (PVP)为分散剂 ,无水乙醇为反应介质 ,偶氮二异丁腈为引发剂 ,采用分散聚合方法 ,制备出球形度良好的单分散聚苯乙烯微球。
补充资料：通用级聚苯乙烯
通用级聚苯乙烯是由苯乙烯单体进行本体或悬浮聚合反应制得。结构式如图。平均分子量(20-30)万。无色透明颗粒，无臭、无味、无毒。具有良好的刚性、光泽性和耐化学性。折射率1. 59-1．60。热变形温度70-98 ℃，使用温度60-80 ℃，脆性温度一30℃。尺寸稳定性好，收缩率约为0．45％。吸湿性低，约为0．02％。溶于丙酮、甲乙酮、苯、甲苯、醛醛乙酯、氯仿、环己烷、二氧六环、吡啶、四氢呋喃、二硫化碳等有机溶剂。不溶于低级醇、乙醚、脂肪烃、某些矿物油、有机酸、碱、元机盐等。容易着色，电性能优良。脆性大，不耐冲击，容易燃烧。
相对密度 1.04～1.09；冲击强度（kJ/m2) 16；弯曲强度＞80MPa；马丁耐热＞68℃。
贮存于阴凉、通风的库房内，防火。