1) ultrasonic melt treatment
超声熔体处理
2) ultrasonic molten melt treatment
超声波金属熔体处理
3) melt superheating treatment
熔体超温处理
1.
It is shown that the deviation angle of the crystal orientation and total content of solutes in interdendritic area are little affected by the melt superheating treatment.
研究了不同熔体超温处理温度对DD3单晶高温合金二次枝晶间距的影响,并利用旋转定向测试法测量单晶取向偏离度结果表明,熔体超温处理对单晶取向偏离度和合金枝间溶质元素总含量的影响很小;随熔体超温处理温度由起始凝固温度1500℃升高至1640和1780℃,二次枝晶间距减小,细化率达14%—31%。
2.
With constant thermal gradient of solid/liquid interface,the influence of the melt superheating treatment on the den- drite arm spacing and microsegregation of DD403 Ni-based single crystal superalloy is studied.
在保持固液界面温度梯度不变的条件下,本文研究了熔体超温处理对 DD403单晶高温合金枝晶间距和显微偏析的影响。
4) ultrasonic treatment
超声处理
1.
Effect of ultrasonic treatment on the electrochemical properties of LiV_3O_8 prepared by hydrothermal reaction;
超声处理对水热合成LiV_3O_8电化学性能的影响
2.
Influence of ultrasonic treatment on properties of hydroxyapatite/gelatin composite material;
超声处理对羟基磷灰石/明胶复合材料性能的影响
3.
Preparation of silver-coated glass fiber by electroless plating with ultrasonic treatment
超声处理化学镀法制备镀银玻璃纤维
5) ultrasonic processing
超声处理
1.
The surface of nano-Sm_2O_3 powders was modified using titanate as coupling agent and ultrasonic processing.
用钛酸酯偶联剂,通过超声处理技术对纳米Sm2O3进行表面改性,并用沉降体积分析,红外光谱分析和TEM分析等手段对改性效果进行表征。
2.
The surface of ~nanoSnO_2 powders was modified by using coupling agent and ~ultrasonic processing.
用超声处理与偶联剂相结合对纳米SnO_2进行表面改性,用沉降体积、激光粒度分析、红外光谱(FT-IR)和透射电镜(TEM)等手段对改性效果进行表征。
3.
Using ultrasonic processing technique to raise the quality of i nt erface between aramid fiber and resin is analyzed deeply.
对芳纶纤维界面的超声处理技术进行了深入的探讨。
6) ultrasonication
[,ʌltrə,sɔni'keiʃən]
超声处理
1.
Will change in ultrasound,we observe that the cell which are dealt with specify ultrasonication are dispersed and the cell wall is broken correspondingly in constrast with referent sample under the microscope.
在光学显微镜下观察发现 ,超声波处理的豆粕与参照组样品比较 ,经过特定超声处理的豆粕样品细胞变散、细胞壁破碎 ,这种状态更有利于细胞内有机物质的提取及有效物质的再利
2.
Preliminary statistical analysis,based AFM images of reduced graphene oxide nanosheets,was performed for investigating the effects of standing-treatment,magnetic stirring,centrifugation,ultrasonication and their sequences to their lateral-dimensions distribution.
利用化学还原法制备了还原氧化石墨烯,基于还原氧化石墨烯的AFM观测结果,初步统计分析了静置、磁力搅拌、离心和超声处理及它们的次序对还原氧化石墨烯横向尺寸分布的影响,结果表明后述3个步骤及次序是影响斑点状(横向尺寸<100nm×100nm)和树叶状(横向尺寸>500nm×500nm)还原氧化石墨烯横向尺寸分布的主要因素。
补充资料：超声处理
分子式：
CAS号：
性质：利用11000～20000Hz的声频(超过人耳可听范围)来破坏细胞(包括细菌)以制备无细胞制剂。也可利用更高频率声频。
CAS号：
性质：利用11000～20000Hz的声频(超过人耳可听范围)来破坏细胞(包括细菌)以制备无细胞制剂。也可利用更高频率声频。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条