1) glass based bone cement
玻璃基生物骨水泥
1.
Research on the formation of nano-size hydroxyapatite in glass based bone cement;
玻璃基生物骨水泥内部纳米羟基磷灰石的形成研究
2) glass-based bone cement
玻璃基骨水泥(GBC)
3) glass based bone cement
玻璃基骨水泥
1.
Microstructure and mechanical properties of glass based bone cement(GBC) were studied.
实验结果表明:通过浸泡于人体模拟液(simulatedbodyfluid,SBF)中,GBC内部会生成具有良好的生物活性类骨状磷灰石(hy droxyapatite,HAP),这些HAP的近似球状和柱状,端面尺寸在30～50nm,且交错生形成玻璃基骨水泥的自固化,提高内部结构的致密性,同时类骨状HAP晶体有利于增强GBC的力学性能。
2.
Microstructure and mechanical properties of glass based bone cement(GBC)were studied.
通过实验研究自固化玻璃基骨水泥(glass based bone cement,GBC)的显微结构及力学性能,讨论了显微结构对GBC 生物活性和力学性能的影响。
4) glass based composites bone cement
玻璃基复合水泥
1.
The glass based composites bone cement which was made from β-tricalcium phosphate and glass based bone cement was immersed in the simulated body fluid, its microstructure and strength were investigated.
在玻璃基水泥中掺加β-磷酸三钙(β-TCP),制成玻璃基复合水泥试样。
5) Cement Glass
水泥玻璃
6) Cement-water glass
水泥-水玻璃
1.
According to geological conditions of different places, different cement-water glass grouting methods were applied respectively.
根据不同地段各种复杂的岩土状况,分别采用不同的水泥-水玻璃注浆工艺,对含水量丰富地段,采用摆喷注浆形成隔水帷幕,从而有效地解决了地层复杂、基岩埋深变化大、含水量丰富的断层地段的地基处理难题,取得了良好的加固效果。
2.
The material property, formula and construction technology of cement-water glass were introduced.
本文介绍水泥-水玻璃材料性质、配方及施工工艺等内容,通过几个典型的工程实例,充分显示水泥-水玻璃化学灌浆在危房纠偏、软土补强、基坑防水等工程地基中的应用前景。
3.
From the practical point of view, feasibility and reliability of the seawall project using cement-water glass reinforcement grouting were analyzed.
从现实出发,分析了海堤工程采用水泥-水玻璃固结注浆的可行性及可靠性,并通过对海堤注浆试验研究了注浆技术参数,包括注浆孔布置参数、注浆压力、注浆段长、注浆材料及配比、特殊情况的处理、注浆结束标准及封孔,以及注浆施工的注浆方法和工艺流程,并对公式计算的理论值与施工中的实际值做了对比分析。
补充资料：聚甲基丙烯酸甲酯-生物活性陶瓷骨水泥
分子式：
CAS号：
性质： 用生物活性陶瓷颗粒增进骨水泥表面的骨传导能力，通过颗粒与长人基体的新骨键合或为新骨所替换而增强骨水泥，从而提高其固结力，增长寿命。该复合材料缺点是初始强度低，目前仅限于在承受低负载的体位使用。
CAS号：
性质： 用生物活性陶瓷颗粒增进骨水泥表面的骨传导能力，通过颗粒与长人基体的新骨键合或为新骨所替换而增强骨水泥，从而提高其固结力，增长寿命。该复合材料缺点是初始强度低，目前仅限于在承受低负载的体位使用。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条