1)  yttrium aluminum garnet
钇铝石榴石粉
2)  Cr-Y-Al red
铬钇铝红
1.
The Cr-Y-Al Red Pigment is a kind of new ceramic pigment that is present itself to the market in recent years.
铬钇铝红是近几年才在市场上出现的一种新型陶瓷色料,其呈色鲜艳、明快,无毒无害,高温下呈色稳定,是其它红色色料如锰红、铬锡红等所不能替代的。
3)  yttrium aluminum garnet
钇铝石榴石
1.
Nano-crystalline yttrium aluminum garnet (YAG) powders were prepared by the co-precipitation method using Al(NO3)3·9H2O and Y(NO3)3·6H2O as raw materials, the NH4HCO3 as precipitator, and (NH4)2SO4 as dispersion medium.
以硝酸铝[Al(NO3)3·9H2O]和硝酸钇[Y(NO3)3·6H2O]为原料、以碳酸氢铵[NH4HCO3]为沉淀剂,硫酸铵[(NH4)2SO4]为分散剂,用共沉淀法合成钇铝石榴石(yttrium aluminumgarnet,YAG)纳米粉体。
2.
Transparent yttrium aluminum garnet (YAG ) ceramics were synthesized by a solid-state reaction method using commercial high-purity ultra-fine powders of α-Al2O3 and Y2O3 as starting materials.
采用高纯α-Al2O3和Y2O3作为原料并由固相反应法合成了钇铝石榴石(yttriumaluminumgarnet,YAG)透明多晶陶瓷。
3.
The powder of yttrium aluminum garnet was synthesis by heating mixture solution and the sol-burning process.
将氧化钇溶解于硝酸溶液中,形成硝酸钇溶液,与硝酸铝混合并加热形成溶胶,在燃烧剂尿素的作用下发生燃烧反应,制备出了钇铝石榴石粉体。
4)  YAG
钇铝石榴石
1.
On the Synthesis of YAG Nanopowders and Fabrication of Transparent YAG Ceramic;
钇铝石榴石纳米粉体及YAG透明陶瓷的制备研究
2.
Oversintered YAG ceramics were synthesized at different sintering rates by solid-state reaction method at 1850℃,and the morphology of YAG ceramics grain boundary changed with different heating rates.
采用固相反应法用不同的烧结速率在1850℃烧结合成过烧钇铝石榴石(YAG)陶瓷,YAG陶瓷晶界形貌随烧结速率的变化而不同。
5)  yttrium aluminium garnet
钇铝石榴石
6)  Yttrium aluminum garnet (YAG)
钇铝柘榴石
参考词条
补充资料：钇-铝石榴石型旋磁铁氧体
分子式：
CAS号：

性质：用三价铝离子置换钇铁石榴石中一部分三价铁离子所形成的旋磁铁氧体。化学式Y3Fe5-xAlxO12。饱和磁化强度0.0225～0.15T。居里温度110～275℃。铁磁共振线宽2.8～6.4kA/m(9kHz)。介电常数11.7～16.0。介质损耗角正切值(2.5～4.0)×10-4。主要原料为三氧化二钇和氧化铝。采用电子陶瓷工艺，热压烧结或氮气氛烧结。随着铝含量的增加，饱和磁化强度和居里温度也随之下降。适用于制作S波段以下的频率范围的钇-铝石榴石型旋磁铁氧体器件。也可制成微带磁性的基片。

说明：补充资料仅用于学习参考，请勿用于其它任何用途。