1) alite-rich clinker
高C3S熟料
2) high intake of C3S clinker
高 C3S 水泥熟料
1.
In this paper, the formation of high intake of C3S clinker under lowertemperature（1450℃） was studied firstly .
本论文从研究利用工业废渣改善水泥生料易烧性入手，运用金相显微镜、X 射线衍射、等离子电感耦合光谱仪、环境扫描电镜和能谱仪等测试方法，对在较低温度（1450℃）下高 C3S 水泥熟料制备和形成机理进行了详细的研究。
3) high C_3S cement
高C3S水泥
1.
In this paper,the effect of the hydration time,the ratio of water to cement and the hydration temperature on the ion concentrations in water extraction solution of high C_3S cement paste has been investigated by water extraction method.
为了研究高C3S水泥硬化浆体水浸取液中离子浓度与水化条件间的关系,本文利用水浸取法探讨了水化时间、水灰比、水化温度等因素对高硅酸三钙水泥水化硬化体系水浸取液中离子浓度的影响。
4) C 3S
C3S
1.
The hydration of pure minerals C 3S and β C 2S were studied at 20 ℃ and 40 ℃ in water vapor .
研究了水泥熟料单矿物C3S、β C2 S分别在 2 0℃和 40℃水蒸气中的水化情况 ,气相相对湿度分别为 99%、97。
2.
The reaction pro perties of C 3S,C 3A with CaCO 3 are also investigated for verification of the mortar test results.
文章还对单矿物C3S、C3A与CaCO3 反应的特点进行了研究 ,以此证实胶砂试验结果。
5) high MgO clinker
高MgO熟料
1.
Discussion on silic module of high MgO clinker;
高MgO熟料硅率的探讨
6) high agglomerate
高熟料比
1.
This paper summarizes the specific technical measures of hot metal output increasing and coke saving on No 1 BF at Sanming Iron and Steel Works The results were obtained mainly by adopting high agglomerate rate,high grade burden,low BF downtime,high top pressure and high blast flow rat
三钢１号高炉增铁节焦的主要措施是高熟料比、高品位、低休风率、高顶压、大风量。
补充资料：高铝矾土熟料
分子式：
CAS号：
性质：经过煅烧的高铝矾土。以氧化铝含量的高低来分级，其煅烧温度根据高铝矾土的等级而定。煅烧后氧化铝的含量在50％～90％之间，主要矿物组成为莫来石、刚玉和玻璃相，有的还有少量石英，各相的含量由铝硅比(Al2O3/SiO2)决定。结构致密、高温体积稳定性好、耐火度高。用于制造高铝质耐火材料的主要原料。也是制造熔炼刚玉系磨料及高铝水泥的原料。中国高铝矾土资源丰富，主要产于山西、河北、河南、山东、贵州及广西等地区。
CAS号：
性质：经过煅烧的高铝矾土。以氧化铝含量的高低来分级，其煅烧温度根据高铝矾土的等级而定。煅烧后氧化铝的含量在50％～90％之间，主要矿物组成为莫来石、刚玉和玻璃相，有的还有少量石英，各相的含量由铝硅比(Al2O3/SiO2)决定。结构致密、高温体积稳定性好、耐火度高。用于制造高铝质耐火材料的主要原料。也是制造熔炼刚玉系磨料及高铝水泥的原料。中国高铝矾土资源丰富，主要产于山西、河北、河南、山东、贵州及广西等地区。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条