1) Aluminum Titanate Ceramic
钛酸铝陶瓷
1.
The Influence of Milling Time on Properities of Aluminum Titanate Ceramic Slip and Fired-Product;
研磨时间对钛酸铝陶瓷泥浆及制品性能的影响
2.
The effects of additives (MgO-Al2O3-SiO2, Al2O3-SiO2, Si3N4, SiC) on properties and structure of hot-pressed aluminum titanate ceramics were studied.
研究了ＭｇＯ－Ａｌ２Ｏ３－ＳｉＯ２、Ａｌ２Ｏ３－ＳｉＯ２、Ｓｉ３Ｎ４、ＳｉＣ四种添加剂对热压钛酸铝陶瓷力学与热学性能的影响。
2) mullite aluminum titanate ceramics
莫来石-钛酸铝陶瓷
4) BaTiO_3 ceramics
钛酸钡陶瓷
1.
BaTiO_3 ceramics with average grain size from 0.
钛酸钡陶瓷介电性能有明显的粒度效应,晶粒在1。
6) strontium titanate ceramics
钛酸锶陶瓷
1.
Some research development on the sintering of strontium titanate ceramics was reviewed,and two major factors that affect the sintering technology and aids were summarized.
钛酸锶陶瓷电容具有高储能、低损耗、高稳定性等优点,但烧结温度高,烧成密度低。
补充资料：钛酸铝陶瓷
分子式：
CAS号：
性质：由1mol氧化铝和1mol氧化钛化合组成的人工合成陶瓷材料。熔点为1860℃，属斜方晶系。主要特性是低的热膨胀系数(0.87×10-6K-1)，低的导热性[1～2W/(m·K)]，高的耐温性(可在1400℃长期工作)，良好的抗蚀性(耐难熔金属如铜水、铝水、铁水的侵蚀)，以及可经受从室温到1400℃熔融铁水环境的热冲击性。通常可采用干压、浇注挤压等工艺成型，在氧化气氛中于1400～1600℃烧结。可以用它制备连续测量熔融金属温度的热电偶保护管，或制备成汽车尾气净化用的蜂窝陶瓷以及发动机排气管的内衬及活塞顶等。
CAS号：
性质：由1mol氧化铝和1mol氧化钛化合组成的人工合成陶瓷材料。熔点为1860℃，属斜方晶系。主要特性是低的热膨胀系数(0.87×10-6K-1)，低的导热性[1～2W/(m·K)]，高的耐温性(可在1400℃长期工作)，良好的抗蚀性(耐难熔金属如铜水、铝水、铁水的侵蚀)，以及可经受从室温到1400℃熔融铁水环境的热冲击性。通常可采用干压、浇注挤压等工艺成型，在氧化气氛中于1400～1600℃烧结。可以用它制备连续测量熔融金属温度的热电偶保护管，或制备成汽车尾气净化用的蜂窝陶瓷以及发动机排气管的内衬及活塞顶等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条