1) sorbite percentage
索氏体含量
2) martensite content
马氏体含量
1.
Study on relationship between properties and martensite content and size of dual-phase steel;
双相碳钢性能与马氏体含量和晶粒大小关系初析
2.
The research results show that the maximum shear stress of dual-phase steel raises with the increase of martensite content.
研究表明,随着马氏体含量的增加,双相钢的最大剪切应力随之增加。
4) bainite content
贝氏体含量
5) low remnant austenite content
低残余奥氏体含量
6) sorbite
['sɔ:bait]
索氏体
1.
The results show that 82B wire rod brittle fracture is mainly caused by excessive inclusion,reticulate carbide,lower sorbite in the microstructure,and surface defect of wire rod.
结果表明,82B钢盘条脆断的主要原因是夹杂物级别超标、组织中出现网状碳化物、索氏体含量偏低以及盘条表面缺陷等。
2.
The technology not only guarantees that there are good microstructures of the tempered troostite and sorbite in the wire rod steel, but also makes environmental pollu.
该工艺在保证盘条钢具有良好的回火屈氏体和索氏体组织外,还减少了对环境的污染和对人体的危害。
3.
It is concluded by the research that the main causes of X82B wire rod brittle fracture are composition segregation、exceeding inclusion、abnormal microstructure、lower sorbite、surface defect of wire rod and bad operation of electric connection.
研究认为:X82B盘条脆断的主要原因是由于成分偏析、夹杂物级别超标、金相组织异常、索氏体含量偏低、盘条表面缺陷及接头不良造成的。
补充资料：索氏体
分子式：
分子量：
CAS号：
性质：钢经正火或等温转变所得到的铁素体与渗碳体的机械混合物。索氏体组织属于珠光体类型的组织，但其组织比珠光体组织细。索氏体具有良好的综合机械性能。将淬火钢在450-600℃进行回火，所得到的索氏体称为回火索氏体（tempered sorbite）。回火索氏体中的碳化物分散度很大，呈球状。故回火索氏体比索氏体具有更好的机械性能。这就是为什么多数结构零件要进行调质处理（淬火+高温回火）的原因。
分子量：
CAS号：
性质：钢经正火或等温转变所得到的铁素体与渗碳体的机械混合物。索氏体组织属于珠光体类型的组织，但其组织比珠光体组织细。索氏体具有良好的综合机械性能。将淬火钢在450-600℃进行回火，所得到的索氏体称为回火索氏体（tempered sorbite）。回火索氏体中的碳化物分散度很大，呈球状。故回火索氏体比索氏体具有更好的机械性能。这就是为什么多数结构零件要进行调质处理（淬火+高温回火）的原因。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。