1) liquefied-bamboo
液化竹材
1.
By reacting liquefied-bamboo(BL) with formaldehyde,a liquefied-bamboo phenol formaldehyde resin adhesive(BLF) of exterior grade could be prepared at phenol/formaldehyde(molar ratio) 1∶1.
液化竹材 (BL)与甲醛反应 ,当液化物中苯酚与甲醛摩尔比 1∶1。
2) liquefied bamboo-formaldehyde resin
液化竹材甲醛树脂
3) bamboo liquefaction phenolic resin
竹材液化物酚醛树脂胶
1.
The curing reaction process of bamboo liquefaction phenolic resin with different molar ratio was studied by non-isothermal differential scanning calorimetry(DSC).
采用非等温差示热量扫描DSC曲线方法探讨了竹材液化物酚醛树脂胶不同物质的量之比时的固化反应过程。
4) Bamboo-softening
竹材软化
5) bamboo chemimechanical pulp
竹材化机浆
1.
The properties of bamboo chemimechanical pulp reinforced thermoplastic composite, such as mechanical properties, thermal properties and processing fluidity, were studied in this paper.
研究竹材化机浆 (CMP)增强尼龙复合材料的力学性能、热学性能、加工性能 ,分析复合材料的界面改性及其微观结构。
补充资料：竹材
| 竹材 bamboo 竹类木质化茎秆部分。有时泛指竹的茎、枝和地下茎的木质化部分。 竹材的利用有原竹利用和加工利用两类。原竹利用时是把大竹用作建筑材料，运输竹筏，输液管道；中、小竹材制作文具、乐器、农具、竹编等。加工利用有多种用途，如竹材层压板可制造机械耐磨零件等；竹木复合板曾制成第一架竹材单翼高级教练机；竹材人造板可作工程材料。此外竹黄还可制成多种工艺美术品。竹材也是造纸、制纤维板和醋酸纤维、硝化纤维的重要原料。竹炭表面硬度高于木炭，可用于冶炼工业和制取活性炭。 竹秆分节，两节之间为节间（见竹）。节间的秆壁横切面自外向内是：表皮、皮下层、皮层、基本薄壁组织（其中有维管束）和髓环。节的维管束向外或向内稍现弯曲，也有进入节隔盘曲复出的。节隔的维管束外缘密，中央疏，直径及方向无定；分成许多细枝，迂回交织成网状，是竹液横向流动的主要通道。节隔的基本薄壁组织的细胞加厚变硬。
竹材的密度因竹龄（成熟的密度较大）、部位（梢段或秆壁外缘密度较大）和竹种而异，平均约0.64克／厘米3。竹材的干缩率低于木材，弦向干缩率最大，径向次之，纵向最小；干燥时失水快而不匀，容易径裂；气干竹材吸水性强。顺纹抗拉强度较高，平均约为木材的2倍，单位重量的抗拉强度约为钢材的3～4倍，顺纹抗剪强度低于木材。强度从竹秆基部向上逐渐提高，并因竹种、年龄和立地条件而异。 竹材的化学成分为：纤维素40％～60％，半纤维素14％～25％或更多，木质素16％～34％，有随年龄增长的趋势。提取物：冷水浸出2.5％～5％，热水浸出5％～12.5％，醇-乙醚浸出3.5％～5.5％，醇-苯浸出2％～9％，1％氢氧化钠浸出21％～31％。此外还有蛋白1.5％～6％，脂肪胶腊2％～4％，淀粉类2％～6％，还原糖约2％，氮0.21％～0.26％，灰分1％～3.5％。所含磷、钾等的总量逐年减少，而硅则有增加，积聚于硅质细胞，竹青中可达4.35％或更多。 |