1) bisphenol A epoxy acrylate resin
双酚A环氧丙烯酸酯树脂
2) Bisphenol A-type epoxy diacrylates resin
环氧丙烯酸双酯树脂
3) DGEBP
双酚丙烯型环氧树脂
4) bisphenol-A epoxide vinylester resin
双酚A环氧乙烯基酯树脂
1.
Resin transfer molding(RTM) mould was manufactured with bisphenol-A epoxide vinylester resin as matrix,poly(vinyl acetate) as low shrinkage additive and glass fiber tricot as reinforcing material,according to the basic requirement of matrix resin of RTM mould.
根据树脂传递模塑(RTM)模具对基体树脂的基本要求,选用双酚A环氧乙烯基酯树脂为基体,聚乙酸乙烯酯为低收缩添加剂,玻璃纤维经编织物为增强材料,并加入相应的助剂,制备了复合材料RTM模具。
5) bisphenol A-epoxy-diacrylate
双酚A-环氧丙烯酸双脂
1.
The material was prepared successfully by the copolymerization of bisphenol A-epoxy-diacrylate with styrene, and represents a type of good lens material, having the following properties:nD=1.
讨论了合成双酚A-环氧丙烯酸双脂单体再与苯乙烯共聚制得的新型光学材料——EA光学塑料的结构确定,主要性能达到n_D=1。
6) o-cresol (2-methylphenol) novolac epoxy acrylate resin
邻甲酚环氧丙烯酸树脂
补充资料：环氧丙烯酸酯树脂
分子式：
CAS号：
性质：是指分子结构上带有环氧基的丙烯酸酯树脂。这类树脂要求在170℃以上的高温下烘烤固化，也可以使用二元羧酸、无机酸、胺或酚类化合物交联固化。此外，环氧基团还可与羧基聚合物或氨基树脂发生交联反应。这类树脂成本较高，单体略带毒性，故在涂料工业中的使用受到限制。
CAS号：
性质：是指分子结构上带有环氧基的丙烯酸酯树脂。这类树脂要求在170℃以上的高温下烘烤固化，也可以使用二元羧酸、无机酸、胺或酚类化合物交联固化。此外，环氧基团还可与羧基聚合物或氨基树脂发生交联反应。这类树脂成本较高，单体略带毒性，故在涂料工业中的使用受到限制。