1) peritectic
[,peri'tektik]
包晶
1.
Peritectic microstructure of fused cast α,β-alumina block
熔铸α,β-Al_2O_3制品的包晶显微结构
2.
The phase selection in the process of non-equilibrium solidification of undercooled peritectic iron-base alloys, copper-base alloys, rare earth superconduction oxides and rare earth permanent-magnet compounds is analys,and is classified into different types based on an analysis of the experimental results.
分析了过冷包晶铁基合金、铜基合金、稀土超导氧化物、稀土永磁化合物非平衡凝固过程中的相选择现象。
3.
37%Cu peritectic alloy has been unidirectionally solidified with a wide range of growth velocities.
３７％Ｃｕ（质量分数）包晶合金的凝固过程及其组织形态。
2) peritectic crystallization
包晶结晶
3) peritectic steel
包晶钢
1.
Higher speed casting practice for low Mn/Si ratio peritectic steel;
高速连铸低锰硅比包晶钢的生产实践
2.
Practice on mould level fluctuation control of vertical-bending type caster in refining peritectic steel;
直弧形铸机生产包晶钢结晶器液面波动的控制
3.
The longitudinal crack rate of peritectic steel is much higher than other steel grades since wide slab was put into production at Wide Plate/Coil Plant.
根据中厚板卷厂连铸宽板坯投产以来的生产实践,包晶钢的纵裂纹发生率远高于其它钢种。
4) peritectic reaction
包晶反应
1.
Delayed Phenomenon of Peritectic Reaction Under Non-equilibrium Cooling
非平衡凝固时包晶反应滞后现象的研究
2.
Through observation of SEM phase micrographs of specimen heat-treated at different conditions,the peritectic reaction μAl.
通过对名义成分为Al11Cr2的铸锭在不同温度下进行退火处理后的金相分析,首次观察到了包晶反应μ-Al4Cr+Lη-Al11Cr2,且证实了共析反应η-Al11Cr2-μAl4Cr+-θAl7Cr的存在。
3.
It is researched the influence of cooling rate and the content of silicon and manganese alloy on peritectic reaction and position of peritectic point in Fe-C alloy.
研究了冷却速率和硅、锰合金元素含量对Fe-C合金的包晶反应和包晶点位置的影响;由于CSP薄板坯冷却速率快,Fe-C相图向左下方移动,包晶反应区域的碳含量为0。
5) peritectic alloy
包晶合金
1.
Morphological stability of coupled growth during directional solidification of eutectic and peritectic alloys;
共晶和包晶合金定向凝固过程中共生生长的形态稳定性
2.
Lamellar structures of rapidly unidirectionally solidified Zn-2%Cu peritectic alloy;
Zn-2%Cu包晶合金快速定向凝固层片状组织
3.
Research of the developments of phase and microstructure selection during directional solidification of peritectic alloys;
定向凝固包晶合金相和微观组织选择研究进展
6) hypo-peritectic steel
亚包晶钢
1.
In order to improve surface quality of hypo-peritectic steel slab cast at high speed,several factors,such as overheat temperature,ratio of manganese and sulphur,temperature of mold copper plate,average heat flux and powder properties are discussed.
为改善亚包晶钢高速浇铸时的表面质量,从过热度、锰硫比、拉速、铜板温度、平均热流和保护渣几个方面进行讨论。
补充资料：包晶
包晶
peritectic
包晶PeritectiC一个液相和一个固相冷却时形成一个固相的恒温可逆反应。这种反应形成的组织即为包晶组织，可用公式51+L禅52表示。式中S，和52为两种不同结构的固溶体，L为液体。在金属中，这种相转变是很普遍的。图为显示包晶反应的部分铜锡丈Cu一S栩合金相图。各种成分的合金从液态冷却，到达包晶水平线(51至L)的范围时，首先从液体中析出固体51，直至包晶温度兀，这时从相图上可见，全部或部分S，固相将被52固相所代替，在多数情况下S:固相是围绕预先存在的51固相形成。按照相图可以调节两种固相的比例。在包晶反应时，固相S，要达到52的成分需通过扩散进行，所以包晶速度是很慢的，通常很少能够反应完全。因此在包晶反应结构中常常包含有固相51的残留部分lrjre‘f士一一川}.1}{l:上生生二伙’日自)(;几7(卜7几印.以几‘川‘肠 包晶反应部分铜锡合盆相图 应用包晶反应可以制作轴承合金。当从液相中首先析出的是较硬的中间相时，进行包晶反应，形成硬度较低的固溶体基体，包围在中间相的周围，形成在软基体上分布有硬粒子的耐磨结构二例如含锑10一12%的锡锑合金.就是利用包晶反应使析出较硬的尸相分布在锡的固溶体基体上而成。利用包晶反应还可以在铸造过程中细化晶粒。如在铝及铝合金中加入少量钦，冷却时形成T主A13，当达到包晶反应温度时，是依附于包晶前形成的细小颗粒的达到细化晶粒的效果。所产生的aTIAI。上形核，相就从而(汪复兴)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。