1) corrosion weight loss
腐蚀失重
1.
The corrosion behavior of 20 steel and 08Cr2AlMo steel in saturated H_2S solution were investigated making use of corrosion weight loss test and slow strain rate tension (SSRT).
采用腐蚀失重及慢应变速率拉伸试验(SSRT)方法,对20钢和08Cr2AlMo钢在饱和H2S水溶液中的腐蚀行为进行了研究。
2.
43 alloy materials in artificial seawater are investigated in this paper by corrosion weight loss test.
43合金的腐蚀失重均随腐蚀时间的延长而直线增加,与温度的关系符合Arrhenius公式,在温度一定时,MgNi合金的腐蚀速率随Ni含量的增加而增大。
2) corrosion weightless rates of reinforcing bar
钢筋腐蚀失重率
3) weight loss corrosion measurement
失重法腐蚀测试
4) corrosion failure
腐蚀失效
1.
Evaluation method for dynamic reliability of offshore platform considering fracture and corrosion failures
考虑断裂和腐蚀失效的海洋平台动态可靠性研究
2.
NiCrBSi alloy welded surfacing coating was prepared on the surface of carbon steel using oxyacetylene flame, and the corrosion failure process of the alloy surfacing coating in 3.
5%NaCl溶液中的腐蚀失效过程。
3.
To survey the situation of corrosion failure about pressure vessels and pipes, more than 400 reports and articles related are collected, which concern petro-chemical industry, chemical industry, petroleum industry.
收集整理近年来有关压力容器管道的腐蚀失效案例,并对其进行了归纳与分析。
补充资料：失重法腐蚀测试
分子式：
CAS号：
性质：根据试样腐蚀前后的重量损失来表征腐蚀速度的一种测试方法。用途广、可靠，是有效的最基本的定量评定方法。在均匀腐蚀的情况下根据失重、面积和试验时间即可计算出平均腐蚀速度，常以g/(m2·h)表示，引入材料的密度后即可换算为平均腐蚀深度，常以mm/a表示。该法的关键操作之一是完全清除表面腐蚀产物而又不损伤基体金属。根据腐蚀速度可作出耐蚀性的分类评级。
CAS号：
性质：根据试样腐蚀前后的重量损失来表征腐蚀速度的一种测试方法。用途广、可靠，是有效的最基本的定量评定方法。在均匀腐蚀的情况下根据失重、面积和试验时间即可计算出平均腐蚀速度，常以g/(m2·h)表示，引入材料的密度后即可换算为平均腐蚀深度，常以mm/a表示。该法的关键操作之一是完全清除表面腐蚀产物而又不损伤基体金属。根据腐蚀速度可作出耐蚀性的分类评级。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条