1) mesophase globule
中间相球体
1.
The producing, growing and combining process of mesophase globule were observed after coal liquefaction products were carbonized in the different temperature.
以不同溶剂、不同反应温度、不同氢初压及不同煤种所制取的煤液化产品为主,观察了这些产品经不同温度炭化后中间相球体的产生、长大及结合过程,并探讨了这些中间相球体的产生和所形成焦炭结构间的关系。
2) mesophase sphere
中间相小球体
1.
Its mechanism is the instable mesophase sphere was formed after the pitch was heated gradually, then transforms needle cokes by coalesence.
针状焦是生产ＵＨＰ电极的重要原料，针状焦的生成机理是沥青经逐渐加温生成不稳定中间相小球体，再经堆积中间相转变为针状焦。
3) meso-sphere
中间相小球体沥青
4) carbon mesophase microbead
碳质中间相小球体
5) mesophase microbead
中间相小球
6) MCMB
中间相炭微球
1.
Research on Preparation and Formation Mechanism of MCMB;
中间相炭微球制备与形成机理的研究
2.
Effects of pre-oxidation and the temperature of heat treatment on composition and microstructure of MCMB
预氧化及热处理温度对中间相炭微球组成和结构的影响
3.
The carbon/graphite molding blocks with high density and strength were prepared from mesocarbon microbeads (MCMB) molded at 100 MPa and then heat-treated.
以中间相炭微球(MCMB)为原料,在100MPa的压力下冷模压成型后,再经过热处理得到高密高强炭/石墨材料。
补充资料：中间相
合金相图中在中间成分区域内形成的均质相。晶体结构一般和组元金属不同,物理、化学和力学性质也迥异。中间相是一类重要的合金相。按照结合键的类型，中间相可以分为离子化合物、共价化合物和金属化合物；按照它们的形成规律和结构、性能特征,又可区分为正常价化合物、电子化合物、 间隙化合物和拓扑密堆相（TCP相）。这些化合物一般具有金属性质,只一部分正常价化合物例外。习惯上中间相又常被称为金属间化合物(in-termetallic compound)。但也有人把成分范围较宽的中间相区分为Ⅱ类固溶体(secondary solid solution)，而用金属间化合物一词专指均质范围比较狭窄，化学计量比较简单的中间相（见合金相）。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。