1) Polystyrene latex
聚苯乙烯乳胶
1.
Polystyrene latex particles were prepared by concentrated emulsion polymerization by using \{CHPO\} TEPA as the redox initiator system and SDS CA as the surfactants.
以过氧化羟基二异丙苯 ( CHPO)和四乙烯五胺 ( TEPA)为氧化 -还原引发剂 ,以十二烷基硫酸钠 ( SDS)为乳化剂 ,十六醇 ( CA)为共乳化剂 ,通过超浓乳液聚合方法制备了聚苯乙烯乳胶粒子 。
2) polystyrene latex particles
聚苯乙烯乳胶粒
1.
Monodisperse polystyrene latex particles were prepared via seed emulsion polymerization route, using polystyrene latex particles with an average grit size of 95.
047的聚苯乙烯乳胶粒为种子,采用种子乳液聚合方法制备出单分散的聚苯乙烯乳胶粒,探讨了控制胶粒粒径大小及分布的方法及制备条件。
4) Polystyrene LPA
聚苯乙烯乳胶凝集试验
1.
Muscovy Duck fibroblast cells and embryo liquid infected with virus were carried out with Polystyrene LPA and were positive.
聚苯乙烯乳胶凝集试验呈阳性，提取病毒接种细胞及尿囊液 ＤＮＡ，用自行设计引物扩增到与设计相符的 ６００ｂｐ片段，克隆至 Ｔ载体，经酶切及序列分析表明我们所分离到的病毒为雏番鸭细小病毒（Ｍｕｓｃｏｖｙ Ｄｕｃｋｉｌｉｎｇ Ｐａｖｏｖｉｒｕｓ，ＭＰＶ）。
5) vinyl polyacetic acid latex
聚乙酸乙烯乳胶
6) poly(butyl acrylate)/polystyrene composite latex
聚丙烯酸丁酯/聚苯乙烯复合胶乳
补充资料：聚苯乙烯/聚乙烯共混物
分子式：
CAS号：
性质：由聚苯乙烯与聚乙烯系列为主组成的共混物，添加少量第三组分，如氢化丁苯嵌段共聚物或接枝共聚物等作增容剂，既有聚苯乙烯良好的成型加工性和刚性，又改善其脆性、应力开裂及耐油性，例如：80份聚苯乙烯与20份聚乙烯共混，加入10份氢化丁苯热塑性弹性体，冲击强度可达36.7kJ/m2，拉伸强度为20.8MPa，可通过机械共混或反应挤出共混制备，用于含油脂较多的食品包装容器，如乳制品包装等方面。
CAS号：
性质：由聚苯乙烯与聚乙烯系列为主组成的共混物，添加少量第三组分，如氢化丁苯嵌段共聚物或接枝共聚物等作增容剂，既有聚苯乙烯良好的成型加工性和刚性，又改善其脆性、应力开裂及耐油性，例如：80份聚苯乙烯与20份聚乙烯共混，加入10份氢化丁苯热塑性弹性体，冲击强度可达36.7kJ/m2，拉伸强度为20.8MPa，可通过机械共混或反应挤出共混制备，用于含油脂较多的食品包装容器，如乳制品包装等方面。