1) Aluminate cement
铝酸盐水泥
1.
Application of aluminate cement on refractory casting;
铝酸盐水泥在耐火浇注料中的应用
2.
Under high temperature,the result shows that fly ash had beautiful crushing strength in aluminate cement.
以铝酸盐水泥、粉煤灰为主要原料制备水泥基多孔防火隔热材料,讨论和分析了粉煤灰掺量对抗压强度的影响,并通过高温试验对比,结果表明,粉煤灰在铝酸盐水泥中具有很好的耐高温性,X-射线衍射分析表明,高温前主要矿相为C3AH6,CAH10,C2AS,CA和α-SiO2,高温后主要矿相为C3AH6,C2AS,CA和α-SiO2,CAH10在高温下分解。
2) Aluminous cement
铝酸盐水泥
1.
In this work, new spinel-containing aluminous cements were synthesized from light-burned dolomite powder and industrial Al2O3 by sintering process.
将轻烧白云石粉和工业氧化铝粉按一定比例配料,采用烧结法制备了含镁铝尖晶石的新型铝酸盐水泥。
2.
A new type of aluminous cement containing magnesium aluminate (MA) spinel was prepared from mixtures of dolomite and alumina by a sintering process.
以白云石和工业Al2O3为原料,采用烧结法制备了含镁铝尖晶石的铝酸盐新型水泥,利用X射线衍射检测了合成产物的物相组成,采用扫描电子显微镜观察了新型铝酸盐水泥中各物相的形貌和能谱分析了成分分布,测量了这种铝酸盐水泥的凝结时间、耐火度以及其所结合的高铝矾土制成的耐火浇注料的早期强度。
3.
In this work,new spinel-containing aluminous cements were synthesized from light-burned dolomite powder and industrial Al2O3 powder by sintering process.
以轻烧白云石粉和工业氧化铝粉为原料,采用烧结法制备了含镁铝尖晶石的新型铝酸盐水泥。
3) phosphoaluminate cement
磷铝酸盐水泥
1.
Study on the interface between phosphoaluminate cement ant natural rock;
磷铝酸盐水泥与天然岩石界面的研究
2.
Effect of Limestine on the hydration properties of phosphoaluminate cement;
石灰石对磷铝酸盐水泥水化性能的影响
3.
The sulfate attack resistance of phosphoaluminate cement (PALC) was studied.
初步研究了磷铝酸盐水泥(phosphoaluminate cement,PALC)的抗硫酸镁侵蚀性能,同时与硅酸盐水泥(portland cement,PC)浆体进行了比较,并利用X射线衍射、核磁共振等测试方法对水泥水化浆体微观组成进行分析。
4) sulphoaluminate cement
硫铝酸盐水泥
1.
A systematic study of autogenously pulverizable sulphoaluminate cement,Part one:Preparation and properties;
自粉化硫铝酸盐水泥系列研究之一——自粉化水泥制备及其性能研究
2.
Research of durability of sulphoaluminate cement based concrete with mineral admixture;
掺合料对硫铝酸盐水泥基混凝土耐久性影响的研究
3.
Influence of several kinds of admixtures on the properties of sulphoaluminate cement;
几种外加剂对硫铝酸盐水泥性能的影响
5) Sulfoaluminate cement
硫铝酸盐水泥
1.
A completely new utilization method for the desulfurization residues is put forward to produce sulfoaluminate cement.
提出了用脱硫灰生产硫铝酸盐水泥的全新利用方式,它能完全利用脱硫灰中的游离CaO、CaCO3、Ca(OH)2和含硫矿物CaSO3与CaSO4,使其转化为水泥熟料矿物,如硫铝酸钙等,还能完全利用脱硫灰中的未燃尽碳,因而能达到物尽其用,是一种全新高效的利用方式。
2.
The stability of sulfoaluminate cement pastes at high temperature was investigated.
针对硫铝酸盐水泥水化产物易转变和国际上对延迟性钙矾石形成和破坏的争议 ,研究了硫铝酸盐水泥在不同温度下的膨胀和性能变化行为 。
3.
Compressive strength of sulfoaluminate cement concrete after hydrothermal curing at different temperatures for 24 h, and that after hydrothermal curing under the same condition as above and then standard curing for 28 d were measured in this study.
研究了硫铝酸盐水泥混凝土在不同温度下经湿热养护24h以及在湿热养护后再继续标养28d强度的变化规律。
6) aluminoferrite cement
铁铝酸盐水泥
1.
Research on aluminoferrite cement for application in light wall panel;
铁铝酸盐水泥在轻质墙板中应用的研究
2.
The anchor cement prepared by high performance aluminoferrite cement has a good quality of early strengh, low expansion, cracking resistance and cor rosion resistance.
利用优质铁铝酸盐水泥熟料配制的锚固水泥具有早强、微膨胀、抗裂性能好、耐腐蚀性强等优点。
补充资料：铝酸盐水泥
分子式：
CAS号：
性质：熟料矿物以铝酸盐为主的水泥。其中主要的品种为矾土水泥，又称高铝水泥。矾土水泥加水后，一天强度可达其标号的90％，可用于紧急抢修工程。矾土水泥不宜用于常温尤其是潮湿环境，更不能用蒸汽养护，严禁电热法施工。矾土水泥水化热大，放热迅速，适于浇筑很薄的构件和寒冷地区施工。在低温和干燥环境下，低水灰比矾土水泥有很强的抗硫酸盐腐蚀的能力。矾土水泥耐火性好，使用不同的耐火骨料时，可用于900～1000℃和1300～1500℃甚至1400～1600℃温度下的耐火混凝土。矾土水泥不得与硅酸盐水泥及其他能析出Ca(OH)2的胶凝材料和含CaO的物质混合使用，否则将引起迅速凝结和强度急剧下降。见高铝水泥
CAS号：
性质：熟料矿物以铝酸盐为主的水泥。其中主要的品种为矾土水泥，又称高铝水泥。矾土水泥加水后，一天强度可达其标号的90％，可用于紧急抢修工程。矾土水泥不宜用于常温尤其是潮湿环境，更不能用蒸汽养护，严禁电热法施工。矾土水泥水化热大，放热迅速，适于浇筑很薄的构件和寒冷地区施工。在低温和干燥环境下，低水灰比矾土水泥有很强的抗硫酸盐腐蚀的能力。矾土水泥耐火性好，使用不同的耐火骨料时，可用于900～1000℃和1300～1500℃甚至1400～1600℃温度下的耐火混凝土。矾土水泥不得与硅酸盐水泥及其他能析出Ca(OH)2的胶凝材料和含CaO的物质混合使用，否则将引起迅速凝结和强度急剧下降。见高铝水泥
说明：补充资料仅用于学习参考，请勿用于其它任何用途。