1.
The results showed that:(1) PVDF /PVA were incompatible blends,new interface microvoid structure was produced as a result of phase separation in PVDF/PVA;(2) With PVA content increased,the water flux of PVDF/PVA blend membrane increased due proba.
结果表明,PVDF/PVA为不相容体系,在成膜过程中产生界面微孔;随PVA含量增加,PVDF/PVA共混膜水通量先增大后减小,在PVDF/PVA为8/2时呈较大值,截留率变化趋势则相反;PVA的存在明显改善了PVDF/PVA共混膜的亲水性,表现为随其含量增加共混膜接触角明显减小;随固含量增加,膜厚度增加,孔隙率降低,水通量减小,截留率升高;添加剂PEG600浓度为6%时,孔隙率高,水通量大,但截留率低;凝固浴种类直接影响膜结构及性能;热处理可完善膜结构从而获得性能更优的膜。
6) interface micro-void
相界面孔
1.
A membrane with interface micro-voids was prepared by melt spinning-drawing process and its structure was investigated thoroughly.
针对以聚丙烯腈为分散相、以高形变性和高回复性的热塑性聚氨酯为基质相的共混物,讨论其相容性、可纺性和拉伸致孔性,并在测试分析的基础上,深入研究了经熔融纺丝—拉伸制成的具有相界面孔分离膜的共混结构。
补充资料：多苯基多亚甲基多异氰酸酯
多苯基多亚甲基多异氰酸酯，简称PAPI，或称粗MDI，浅黄色至褐色粘稠液体．有刺激性气味。相对密度(20℃／20 ℃)1．2，燃点218℃。PAPI实际上是由50％MDI与50％官能度大于2以上的多异氰酸酯组成的混合物。升温时能发生自聚作用。溶于氯苯、邻二氯苯、甲苯等。PAPI的活性低，蒸气压低，只是TDI的百分之一，故毒性很低。
用于制造聚氨脂胶粘剂。也可直接加入橡胶胶粘剂中，改善橡胶与尼龙或聚酯线的粘接性能。贮存于阴凉、通风、干燥的库房内，远离火种、热源。严格防水、防潮，避免光照。
用于制造聚氨脂胶粘剂。也可直接加入橡胶胶粘剂中，改善橡胶与尼龙或聚酯线的粘接性能。贮存于阴凉、通风、干燥的库房内，远离火种、热源。严格防水、防潮，避免光照。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条