1) SiC aqueous suspension
SiC水悬浮液
1.
By choosing nanoSiC as the raw material,1 vol% nanoSiC aqueous suspension is obtained by using stabilization mechanisms including single electrostatic, steric ( by PEG ) and electrosteric ( by PMAA-NH4)respectively.
选用纳米粉SiC为原料,分别采用单一静电稳定机制、加入PEG的空间位阻稳定机制和加入PMAA-NH4的电空间稳定机制,制备成1vol%的SiC水悬浮液。
2.
1vol% nano-SiC aqueous suspensions were obtained by different colloidal stabilization mechanism including singleekectrostatic, steric( by PEG ) and electrosteric( by PMAA-NH_4).
选用纳米级SiC颗粒为原料 ,分别采用单一静电稳定机制、加入PEG的空间位阻稳定机制和加入PMAA-NH4的电空间稳定机制 ,制备固相体积分数为 1vol%的SiC水悬浮液 ,通过Zeta电位、沉降实验和粘度测定及粒度分析等手段 ,最终分别获得了碱性条件下高分散、高稳定的SiC水悬浮液 。
2) SiC suspension
SiC悬浮液
1.
Influence of pH, tetramethyl ammonium hydroxide (TMAH), ionic strength and alkali treatment on the rheological properties of aqueous SiC suspensions was investigated.
研究了pH、四甲基氢氧化铵(TMAH)、离子强度及碱处理对水基SiC悬浮液流变性的影响。
3) aqueous suspension
水悬浮液
1.
Study of Nanometer Powder Aqueous Suspension and Application of it in Exterior Coatings;
纳米粉体水悬浮液的制备及其在外墙涂料中的应用研究
2.
Pre-dispersed nano-sized TiO2 aqueous suspension is requiredduring the preparation of nano-composite latex paints.
纳米TiO2复合乳胶漆的制备一般要求预先分散纳米TiO2并制成水悬浮液。
4) aqueous suspension route
水悬浮液法
1.
Bi_8V_2O_(17) pigments were prepared as new ecological colorant pigments by two methods, ceramic route and aqueous suspension route.
用粉末煅烧法和水悬浮液法研制了Bi8V2O17颜料。
5) ZrO2 liquor
ZrO2水悬浮液
1.
By adopting electrostatic stabilization,steric stabilization with PEG and electrosteric stabilization with PMAA-NH4,2vol%ZrO2 liquor was prepared.
本文选用纳米粉ZrO2,分别采用单一静电稳定机制、加入PEG的空间位阻稳定机制和加入PMAA-NH4的电空间稳定机制制备成2vol%的ZrO2水悬浮液,通过Zeta电位、沉降实验等手段,最终得到了碱性条件下的高分散、高稳定的ZrO2水悬浮液。
补充资料：悬浮液
分子式：
CAS号：
性质：又称悬浊液。固体微粒分散于液体中，因布朗运动而不很快下沉，称为悬浮液。悬浮液粒子的直径为10-4～10-3cm，大于胶体。如墨汁、泥浆等。制备悬浮液时通常可加入分散剂，使悬浮稳定。分散剂的作用多半为调节介质黏度或界面膜性质，阻碍粒子接近粘并。
CAS号：
性质：又称悬浊液。固体微粒分散于液体中，因布朗运动而不很快下沉，称为悬浮液。悬浮液粒子的直径为10-4～10-3cm，大于胶体。如墨汁、泥浆等。制备悬浮液时通常可加入分散剂，使悬浮稳定。分散剂的作用多半为调节介质黏度或界面膜性质，阻碍粒子接近粘并。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条