1) urea-formaldehyde
脲醛胶
1.
Ways to modify the gels of polyvinyl formal,polyvinyl acetate,urea-formaldehyde and amylum are plesented and formulae and alternate properties of various modified products introduced.
讨论了聚乙烯醇缩甲醛胶、聚醋酸乙烯酯胶、脲醛胶、淀粉胶的改性途径，介绍了各改性产品的配方及其性能比较。
2) UF glue
脲醛胶
1.
The characteristics, application, development and the control of several key steps in the production of low toxicity, high strength and age resistant UF glue are reviewed.
介绍了脲醛树脂的特点、应用以及生产低毒高强耐老化脲醛树脂过程中几个关键步骤的控制 ,同时介绍了国内外最新发展情况 ,并对低毒高强耐老化脲醛胶在我国的发展前景提出了几点意见。
2.
It can be used for the additive of UF glue after being crushed into powder over 200 mesh.
试验研究表明:山楂核粉在脲醛胶中的分散稳定性比面粉差,单独使用时胶合板板坯的预压性能不理想,与面粉混合使用可以满足预压工艺要求;山楂核粉可以显著地提高脲醛胶的胶合强度,当添加量为胶液10%~15%时,胶合板胶合强度提高幅度最大;山楂核粉具有降低脲醛胶胶合板甲醛释放量的作用,且其作用效果优于面粉。
3) UF resin
脲醛树脂胶
1.
An account is given of the requirements for equipment,adhesive,particle preparation,hot-pressing technology and testing methods when producing Grade E_1 particleboard with E_1 UF resin.
介绍在采用E_1级脲醛树脂胶的情况下,生产E_1级刨花板对设备、胶粘剂、刨花制备、热压工艺及检测的要求。
2.
This paper states that low quality raw material and improper technique proceeding are main factors of affecting product reserving property in preparing UF resin.
本文阐述了在制备脲醛树脂胶的过程中 ,质量较差的原材料和不当的工艺过程 ,是影响成品贮存性的主要因素 ,指出防止生产中出现凝胶等问题的措施。
3.
lt studies the structure and glue property of Salix mongolia, and low poison UF resin used in particleboard of Solix Mongolia.
通过试验分析了脲醛树脂胶中尿素与甲醛的摩尔比与树脂性能的关系；浓缩处理与树脂中游离甲醛含量的关系。
4) UF resin adhesive
脲醛树脂胶
1.
The effect of the molar ratio of formaldehyde to urea on the properties of UF resin adhesive and particleboard was investigated.
本文探讨了脲醛树脂胶中甲醛与尿素摩尔比(F/U)对胶粘剂和刨花板性能的影响,从而优选出生产E1级刨花板所用的胶粘剂。
2.
The paste formation of UF resin adhesive with low formaldehyde/urea molar ratio indicates the synthesis failure of the resin.
采用低摩尔比合成工艺的脲醛树脂胶产生糊化现象，原因在于加成反应阶段，因介质ｐＨ值低，生成了亚甲基脲不溶物，羟甲基化不能充分，它表明此次树脂胜的合成是失败的。
5) urea-formaldehyde resin adhesive
脲醛树脂胶
1.
Synthesis of environment protection type urea-formaldehyde resin adhesive;
环保型脲醛树脂胶的合成
2.
Development of the low cost urea-formaldehyde resin adhesive;
低成本脲醛树脂胶粘剂的研制
3.
The three main adhesives for artificial plate are urea-formaldehyde resin adhesive, phenolic-formaldehyde resin adhesive and melamine-formaldehyde resin adhensive.
人造板工业使用的三大胶是脲醛树脂胶、酚醛树脂胶和三聚氰胺-甲醛树脂胶。
6) urea-formaldehyde adhesive
脲醛胶粘剂
1.
Urea-formaldehyde adhesive with free formaldehyde content lower than 0.
本文研究了脲醛胶粘剂的合成新工艺。
补充资料：脲醛树脂胶黏剂
分子式：
CAS号：
性质：尿素和甲醛反应生成的水溶性初期缩合物。作胶黏剂时，主要用于胶合板生产。典型胶的浓度约50%，含10～20份小麦粉，固化剂氯化铵1～2份。粘接单板，冷压1h后110～120℃热压，热压时间随胶合板厚度而定。脲醛树脂胶黏剂还用于碎料板生产和木工。木工用的是浓度65～70%的胶。脲醛树脂胶黏剂有各种改性方法，如尿素与甲醛反应时拼用聚乙烯醇和甲醇，使黏度上升，稳定性提高。添加尿素、蛋白质等捕醛剂减少残存甲醛含量。添加玻璃粉等耗酸的填料提高胶的耐老化性。本工用胶还常与醋酸乙烯树脂乳液并用，提高性能。脲醛胶黏剂也有粉状供应。
CAS号：
性质：尿素和甲醛反应生成的水溶性初期缩合物。作胶黏剂时，主要用于胶合板生产。典型胶的浓度约50%，含10～20份小麦粉，固化剂氯化铵1～2份。粘接单板，冷压1h后110～120℃热压，热压时间随胶合板厚度而定。脲醛树脂胶黏剂还用于碎料板生产和木工。木工用的是浓度65～70%的胶。脲醛树脂胶黏剂有各种改性方法，如尿素与甲醛反应时拼用聚乙烯醇和甲醇，使黏度上升，稳定性提高。添加尿素、蛋白质等捕醛剂减少残存甲醛含量。添加玻璃粉等耗酸的填料提高胶的耐老化性。本工用胶还常与醋酸乙烯树脂乳液并用，提高性能。脲醛胶黏剂也有粉状供应。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。