1) carbon black filled powdered polychloroprene rubber
SRF填充型粉末氯丁橡胶
2) extended powdered polychloroprene rubber
填充型粉末氯丁橡胶
1.
Rheological property of SRF extended powdered polychloroprene rubber;
SRF填充型粉末氯丁橡胶的混炼流变性能
3) carbon black filled non-sulfur modified powdered polychloroprene rubber
填充型非硫调节型粉末氯丁橡胶
1.
The structure and properties of rare earth modified carbon black filled non-sulfur modified powdered polychloroprene rubber;
稀土掺杂炭黑填充型非硫调节型粉末氯丁橡胶的性能与结构
4) filled powdered styrene-butadiene rubber
填充型粉末丁苯橡胶
5) filler filled powdered rubber
填充型粉末橡胶
1.
The application of Brabender plasticorder in internal mastication,mixing,scorching,and extruding of rubber compounds were reviewed in the paper,based on the evaluation of the processing properties of filler filled powdered rubber.
以填充型粉末橡胶的加工性能评价为例,综述了Brabender转矩流变仪在橡胶的密炼机塑炼、混炼、焦烧模拟、挤出等加工性能表征中的应用。
6) carbon black filled powdered natural rubber
填充型粉末天然橡胶
1.
Rare earth modified carbon black filled powdered natural rubber (Ⅱ) characterization and powdering mechanism
稀土掺杂炭黑填充型粉末天然橡胶 (Ⅱ)微观结构与成粉机理
2.
Rare-earth modified carbon black filled powdered natural rubber (Ⅰ) Particle size distribution
稀土掺杂炭黑填充型粉末天然橡胶 (Ⅰ)制备与粒径分布
补充资料：氯丁橡胶
氯丁橡胶均以乳液聚合法生产，生产工艺流程多为单釜间歇聚合。聚合温度多控制在40～60℃，转化率则在90％左右。聚合温度、最终转化率过高或聚合过程中进入空气（氧气）均会导致产品质量下降。生产中用硫磺－秋兰姆（四烷基甲氨基硫羰二硫化物）体系调节分子量。硫磺－秋兰姆体系的主要缺点在于硫键不够稳定，这是影响贮存性的重要原因之一。若用硫醇调节分子量，则可改善此种性能。氯丁橡胶与一般合成橡胶不同，它不用硫磺硫化，而是用氧化锌、氧化镁等硫化。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。