1) transverse tensile strength
横向拉伸强度
1.
The effects of different process conditions(such as time,temperature,pressure)and volume content of Kevlar on the transverse tensile strength of the composites were discussed.
本文主要对芳纶 /聚丙烯混纤复合材料的横向拉伸性能进行了研究 ,讨论了不同的加工条件 (成型温度、时间、压力 )以及芳纶的体积含量等对复合材料体系横向拉伸强度的影
2.
The effects of different process conditions(such as impregnating time, molding temperature and pressure) and volume content of kevlar on the transverse tensile strength of the composites were discussed.
对单向聚丙烯/芳纶纤维复合材料的横向拉伸性能进行了研究,讨论了压制时间、成型温度、成型压力,以及芳纶纤维的体积含量等对复合材料体系横向拉伸强度的影响。
3.
The effects of different process conditions(such as time,temperature, pressure) and volume content of kevlar fiber on the transverse tensile strength of the composites were discussed.
本文主要对芳纶/聚丙烯混纤复合材料的横向拉伸性能进行了研究,讨论了不同的加工条件(成型温度、时间、压力)以及芳纶的体积含量等对复合材料体系横向拉伸强度的影响。
2) in situ transverse tensile strength
就位横向拉伸强度
1.
A direct relation between the in situ transverse tensile strength and the 90 deg.
本文利用弹性力学和断裂力学方法对纤维增强复合材料的横向拉伸强度进行了理论分析，其中考虑了９０度开裂层厚度和开裂邻层约束效应的影响，推导出正交各向异性对称铺层中复合材料就位横向拉伸强度的数学表达式，得出开裂层的厚度和约束邻层铺设角对就位横向拉伸强度都有影响的结论。
3) transverse stretching
横向拉伸
1.
Finite element analysis and experimental study on transverse stretching deformation behavior of biaxially stretched PTFE membrane;
PTFE薄膜横向拉伸变形行为及其有限元分析
4) biaxial tensile strength
双向拉伸强度
1.
This paper introduces recent studies on biaxial tensile strength of portland cement concrete, which indicate that the biaxial tensile strength is 15%～30% lower than the uniaxial tensile strength.
介绍了"砼双向拉伸强度的研究近况及研究结果,即砼的双向拉伸强度比其单向拉伸强度弱化15%～30%"。
2.
The focal point of this paper is to introduce that the important results of the concrete biaxial tensile strength as well as the application of above results to the thickness design of cement concrete pavement.
主要介绍了水泥砼双向拉伸强度研究的重要结果及其在路面板厚度设计中的应用研究;通过对路面开裂、断板等病害的分析,提出了以砼双向拉伸强度为验算标准的路面板厚度设计建议。
5) hoop tensile strength
环向拉伸强度
1.
The existing shortcoming in the test method of hoop tensile strength of RPM pipes with strip-shape sample are discussed in this paper.
针对RPM管环向拉伸强度测试中采用板条状试样所存在的问题 ,理论分析和试验研究表明通过改变试样形状和尺寸可明显改善测试结果。
6) Radial drawing strength
径向拉伸强度
补充资料：干态拉伸强度
分子式：
CAS号：
性质：又称干态拉伸强度。在规定条件下，以胶黏剂胶接成的制件在干燥后或试片经状态调节后，立即测得的胶接强度。利用测量胶黏剂的干强度可以提供出胶黏剂是否符合标准要求，而且在实际应用时，该指标更能反映出被黏制件经黏结后能否达到使用要求。
CAS号：
性质：又称干态拉伸强度。在规定条件下，以胶黏剂胶接成的制件在干燥后或试片经状态调节后，立即测得的胶接强度。利用测量胶黏剂的干强度可以提供出胶黏剂是否符合标准要求，而且在实际应用时，该指标更能反映出被黏制件经黏结后能否达到使用要求。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条