1) Fe-Ni base superalloy
Fe-Ni基高温合金
2) Ni-Cr-Fe high temperature alloy
Ni-Cr-Fe系高温合金
3) Fe-Ni base alloy
Fe-Ni基合金
1.
Effects of B on the microstructure and hydrogen resistance performance in an Fe-Ni base alloy were investigated by means of optical microscopy,scanning electron microscopy,thermal hydrogen charging experiments and tensile tests.
利用金相显微镜、扫描电镜观察结合力学性能和抗氢性能测试研究了B对Fe-Ni基合金显微组织和抗氢性能的影响。
4) Ni-Fe based alloy
Ni-Fe基合金
5) Fe-based superalloy
Fe基高温合金
6) Ni-base superalloy
Ni基高温合金
1.
Desulphurization during VIM of Ni-base superalloy;
Ni基高温合金真空感应熔炼脱硫
2.
NiCrAlY coatings were prepared on the cast Ni-base superalloy K17 using arc ion plating.
采用电弧离子镀技术在铸造Ni基高温合金K17上沉积NiCrAlY涂层 ,测定了K17合金和NiCrAlY涂层在90 0℃～ 110 0℃的氧化动力学曲线 。
3.
The reduction of sulfur content during the VIM of Ni-base superalloy was studied using CaO crucible, where the role of Al addition in desulphurization was analyzed.
研究了使用CaO坩埚真空感应熔炼炼Ni基高温合金过程中的脱硫情况;分析了加Al的脱硫作用;结合坩埚壁的XRD分析和成分分析数据讨论了CaO坩埚脱硫机理;对CaO坩埚内壁表面发生的化学反应进行了初步热力学计算和讨论。
补充资料：Fe3Al基金属间化合物高温合金
Fe3Al基金属间化合物高温合金
Fe_(3)Al-base intermetallic compound superalloy
Fe3AI JIJ一nshujlon huahewu gaowen heJinFe3AI基金属间化合物高温合金(F e3AI一baseintermetallie eomPound suPeralloy)以Fe3AI相为基体的金属间化合物高温合金。该合金具有优异的高温抗氧化、抗硫化腐蚀性能，合金密度较小，因为不含贵重元素，故价格低廉，很适合于在高温氧化、硫化腐蚀的环境中工作。Fe3AI合金有两个不足之处:室温很脆，伸长率仅3%左右;高温强度不足。通过添加合金元素铬、硼，采取温加工工艺和合理的热处理制度，基本上解决了室温脆性问题，室温拉伸伸长率提高到15%左右。提高强度的途径是进行合金化，添加错、妮、铝等元素进行固溶强化和析出第二相进行时效强化，使合金室温拉伸强度达到l000MPa，600℃拉伸强度达到560MPa。Fe3AI基金属间化合物高温合金可以制造加热元件、炉子紧固件、热交换器、汽车用管材、石油管道和磁性元件等。该合金在真正走向实用之前，应在冶炼工艺和热加工工艺方面进行改进。 (}马培立卜