1) crosslinked polyvinyl alcohol
交联聚乙烯醇
1.
The chemically crosslinked polyvinyl alcohol (CCPVA) studied is prepared by crosslinking PVA in aqueous solution at 50℃ and pH<5 (at later stage )through covalent bonds and contains bactericide and stabilizer.
所研究的化学交联聚乙烯醇 (PVA) ,为PVA与形成共价键的交联剂在 5 0℃、后期 pH值 <5的条件下在水溶液中反应生成的 ,相对分子质量 3。
2.
A novel adsorbent for the adsorption of triglyceride(TG) was prepared by immobilizing sulfanilic acid onto the crosslinked polyvinyl alcohol based bead.
以交联聚乙烯醇凝胶为载体合成了含有对氨基苯磺酸功能基的吸附剂。
2) Crosslinked PVA
交联聚乙烯醇
1.
Separation of Water-Ethylene Glycol Using Crosslinked PVA Membrane:Relationship between the Selective Sorption and the Selective Permeation;
交联聚乙烯醇膜渗透蒸发分离乙二醇－水混合物的溶解选择性与渗透选择性的关系
2.
The swelling equilibrium for the system water－ethylene glycol-crosslinked PVA at various temperatures were experimentally investigated.
对交联聚乙烯醇均质膜于全浓度范围的乙二醇／水溶液中分别在60、70和80℃下进行了溶胀平衡实验研究。
3) Cross-linked poly(vinyl alcohol)
交联聚乙烯醇
1.
The separation of proteins on an anion exchange resin (DEA -PVT) containing diethylamino groups supported by cross-linked poly(vinyl alcohol) was investigated under different conditions.
与载体交联聚乙烯醇相比，ＤＥＡ—ＰＶＴ对蛋白质的非特异性吸附明显降低。
4) PVA crosslinking membrane
聚乙烯醇交联膜
5) Cross-linked polyvinyl alcohol derivative
交联聚乙烯醇衍生物
6) Cross-linked polyvinylcohol del
交联聚乙烯醇水凝胶
补充资料：辐射交联聚乙烯
分子式：
分子量：
CAS号：
性质：交联聚乙烯的一种。密度0.92。热变形温度（1.87兆帕）38~79℃，连续耐热达135℃。体积电阻率>1015欧姆·厘米，介电常数2.27~7.60，介电损耗角正切0.003~0.005。击穿电压（厚3.2毫米）230~1420伏/毫米，吸水率0.01%~0.06%。可用作耐高电压、耐高频的耐热绝缘材料，用于包覆电缆电线，也可用于热收缩薄膜和套管。以高能射线：如β射线、γ射线等辐射聚乙烯使之发生交联而得。
分子量：
CAS号：
性质：交联聚乙烯的一种。密度0.92。热变形温度（1.87兆帕）38~79℃，连续耐热达135℃。体积电阻率>1015欧姆·厘米，介电常数2.27~7.60，介电损耗角正切0.003~0.005。击穿电压（厚3.2毫米）230~1420伏/毫米，吸水率0.01%~0.06%。可用作耐高电压、耐高频的耐热绝缘材料，用于包覆电缆电线，也可用于热收缩薄膜和套管。以高能射线：如β射线、γ射线等辐射聚乙烯使之发生交联而得。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。