说明:双击或选中下面任意单词,将显示该词的音标、读音、翻译等;选中中文或多个词,将显示翻译。
您的位置:首页 -> 词典 -> 2.25Cr-1Mo不锈复合钢
1)  compound steel2.25Cr-1Mo and stainless steel
2.25Cr-1Mo不锈复合钢
2)  Alloy Steel 2.25Cr-1Mo
2.25Cr-1Mo合金钢
1.
A Study on Temper Embrittlement Overaging Phenomenon of Alloy Steel 2.25Cr-1Mo;
2.25Cr-1Mo合金钢回火脆化过时效现象的研究
3)  2.25Cr-1Mo steel
2.25Cr-1Mo钢
1.
Method of Auger electron spectroscopy analysis and its application for temper embrittlement of 2.25Cr-1Mo steels;
Auger电子能谱分析方法及其在2.25Cr-1Mo钢回火脆性中的应用
2.
Heat Treatment of 2.25Cr-1Mo Steel Forgings Used for Hydrogenation Reaction Chamber;
加氢反应器用2.25Cr-1Mo钢锻件的热处理
4)  Cr-1Mo steel
2.25Cr-1Mo钢
1.
Influence of normalizing rate of cooling on mechanical characterics of 2.25Cr-1Mo steel submerged arc welded joints;
埋弧焊条件下冷却速度对2.25Cr-1Mo钢接头性能的影响
5)  Cr-1Mo-0.25V steel
2.25Cr-1Mo-0.25V钢
6)  2.25Cr-1Mo heat-resistant steel
2.25Cr-1Mo耐热钢
补充资料:45钢和40Cr钢调质的热处理工艺
45钢40Cr钢调质                         
    调质是淬火加高温回火的双重热处理,其目的是使工件具有良好的综合机械性能。
    调质钢有碳素调质钢和合金调质钢二大类,不管是碳钢还是合金钢,其含碳量控制比较严格。如果含碳量过高,调质后工件的强度虽高,但韧性不够,如含碳量过低,韧性提高而强度不足。为使调质件得到好的综合性能,一般含碳量控制在0.30~0.50%。

    调质淬火时,要求工件整个截面淬透,使工件得到以细针状淬火马氏体为主的显微组织。通过高温回火,得到以均匀回火索氏体为主的显微组织。小型工厂不可能每炉搞金相分析,一般只作硬度测试,这就是说,淬火后的硬度必须达到该材料的淬火硬度,回火后硬度按图要求来检查。 

工件调质处理的操作,必须严格按工艺文件执行,我们只是对操作过程中如何实施工艺提些看法。


   1、 45钢的调质
   45钢是中碳结构钢,冷热加工性能都不错,机械性能较好,且价格低、来源广,所以应用广泛。它的最大弱点是淬透性低,截面尺寸大和要求比较高的工件不宜采用。


   45钢淬火温度在A3+(30~50) ℃,在实际操作中,一般是取上限的。偏高的淬火温度可以使工件加热速度加快,表面氧化减少,且能提高工效。为使工件的奥氏体均匀化,就需要足够的保温时间。如果实际装炉量大,就需适当延长保温时间。不然,可能会出现因加热不均匀造成硬度不足的现象。但保温时间过长,也会也出现晶粒粗大,氧化脱碳严重的弊病,影响淬火质量。我们认为,如装炉量大于工艺文件的规定,加热保温时间需延长1/5。


   因为45钢淬透性低,故应采用冷却速度大的10%盐水溶液。工件入水后,应该淬透,但不是冷透,如果工件在盐水中冷透,就有可能使工件开裂,这是因为当工件冷却到180℃左右时,奥氏体迅速转变为马氏体造成过大的组织应力所致。因此,当淬火工件快冷到该温度区域,就应采取缓冷的方法。由于出水温度难以掌握,须凭经验操作,当水中的工件抖动停止,即可出水空冷(如能油冷更好)。另外,工件入水宜动不宜静,应按照工件的几何形状,作规则运动。静止的冷却介质加上静止的工件,导致硬度不均匀,应力不均匀而使工件变形大,甚至开裂。